WO2005090635A1 - Alumina coating, coated product and method of making the same - Google Patents
Alumina coating, coated product and method of making the same Download PDFInfo
- Publication number
- WO2005090635A1 WO2005090635A1 PCT/US2005/008012 US2005008012W WO2005090635A1 WO 2005090635 A1 WO2005090635 A1 WO 2005090635A1 US 2005008012 W US2005008012 W US 2005008012W WO 2005090635 A1 WO2005090635 A1 WO 2005090635A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating layer
- alumina
- coating
- substrate
- kappa
- Prior art date
Abstract
Description
Claims