WO2006035200A1

WO2006035200A1 - Zeolite compositions for lowering maximum cementing temperature

Info

Publication number: WO2006035200A1
Application number: PCT/GB2005/003610
Authority: WO
Inventors: Karen Luke; Russell M. Fitzgerald; Frank Zamora; Joe M. Sandy
Original assignee: Halliburton Energy Services, Inc.; Wain, Christopher, Paul
Priority date: 2004-09-29
Filing date: 2005-09-20
Publication date: 2006-04-06
Also published as: US20060065399A1; CA2580527A1; CA2580527C; US7219733B2

Abstract

Zeolite compositions having a low maximum setting temperature for use in permafrost and waterwell applications are provided.

Description

ZEOLITE COMPOSITIONS FOR LOWERING MAXIMUM CEMENTING

TEMPERATURE

Background

Conventionally, a wellbore is drilled using a drilling fluid that is continuously circulated down a drill pipe, through a drill bit, and upwardly through the wellbore to the surface. The next operation usually involves running a pipe string, e.g., casing, into the wellbore, and then cleaning out the wellbore, after which primary cementing operations are typically performed. The pipe is cemented in the wellbore by placing a cement slurry in the annulus between the pipe and the walls of the wellbore. The cement slurry sets into a hard impermeable mass, and is intended to bond the pipe to the walls of the wellbore whereby the annulus is sealed and fluid communication between subterranean zones or to the surface by way of the annulus is prevented.

During any of the above or other operations performed in the wellbore, a number of problems can occur, some of which are caused by the increased temperature achieved by the setting of the cement slurry, particularly in applications involving a permafrost environment or in a waterwell environment. The heat of hydration of cement is the heat generated when water (or a carrier fluid) and portland cement react. Hydration of the tricalcium silicate and tricalcium aluminate components, particularly the tricalcium aluminate, of portland cements produces an exothermic reaction that generates heat. In most cement structures, the resulting temperature increase is small because the heat is dissipated rapidly from exposed surfaces. However, in permafrost applications, dissipated heat from the setting of cement can cause damage to the surrounding environment by softening or melting the permafrost. Further, in waterwell applications where PVC pipe is used for casing, the dissipated heat can damage the pipe by softening or melting the PVC.

Brief Description of the Drawings

FIG. 1 is a plot of temperature vs. time of setting for cement composition 1;

FIG. 2 is a plot of temperature vs. time of setting for cement and zeolite composition 2;

FIG.3 is a plot of temperature vs. time of setting for fly ash composition 3; and

FIG. 4 is a plot of temperature vs. time of setting for fly ash and zeolite composition 4; Description

The present embodiments relate to cementitious compositions containing zeolite that are designed for low maximum temperature of setting for applications that benefit from such low temperature setting such as in permafrost applications and in waterwell applications. In addition, the compositions of the present embodiments include zeolite and have higher compressive strength as compared to cementitious compositions that do not include zeolite. In particular, compositions of the present embodiments that include cement and zeolite demonstrate a reduction of 25 ⁰F (13.9 ⁰C) in the maximum temperature reached during setting compared to a cement composition that does not include zeolite. Further, compositions of the present embodiments that include zeolite and fly ash demonstrate a reduction of 41.4 ⁰F (23 ⁰C) in the maximum temperature reached during setting compared to a composition of fly ash that does not include zeolite. For the compositions of the present embodiments that contain zeolite and cement, and zeolite and fly ash, the compressive strength for a 72 hour set time was increased 55% and 354%, respectively as compared to compositions of cement and fly ash, respectively, that do not include zeolite.

A method of performing a cementing operation in a permafrost zone or a waterwell zone, the zone penetrated by a wellbore, is an embodiment of the present invention. The method comprises placing a cementitious composition into the zone, the cementitious composition comprising a base mix of cementitious material and zeolite, and a carrier fluid; and allowing the cementitious composition to set therein. The cementing operation may be primary or remedial cementing.

Zeolites: Zeolites are porous alumino-silicate minerals that may be either a natural or manmade material. Manmade zeolites are based on the same type of structural cell as natural zeolites, and are composed of aluminosilicate hydrates having the same basic formula as given below. It is understood that as used in this application, the term "zeolite" means and encompasses all natural and manmade forms of zeolites. All zeolites are composed of a three-dimensional framework of SiO₄ and AlO₄ in a tetrahedron, which creates a very high surface area. Cations and water molecules are entrained into the framework. Thus, all zeolites may be represented by the crystallographic unit cell formula:

M_37nKAlO₂USiO₂)J ^• xH₂O.

M represents one or more cations such as Na, K, Mg, Ca, Sr, Li or Ba for natural zeolites and NH₄, CH₃NH₃, (CH₃)₃NH, (CH₃)₄N, Ga, Ge and P for manmade zeolites; n represents the cation valence; the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5; and x represents the moles of water entrained into the zeolite framework.

Zeolites for use in the compositions of the present embodiments include analcime (hydrated sodium aluminum silicate), bikitaite (lithium aluminum silicate), brewsterite (hydrated strontium barium calcium aluminum silicate), chabazite (hydrated calcium aluminum silicate), clinoptilolite (hydrated sodium aluminum silicate), faujasite (hydrated sodium potassium calcium magnesium aluminum silicate), harmotome (hydrated barium aluminum silicate), heulandite (hydrated sodium calcium aluminum silicate), laumontite (hydrated calcium aluminum silicate), mesolite (hydrated sodium calcium aluminum silicate), natrolite (hydrated sodium aluminum silicate), paulingite (hydrated potassium sodium calcium barium aluminum silicate), phillipsite (hydrated potassium sodium calcium aluminum silicate), scolecite (hydrated calcium aluminum silicate), stellerite (hydrated calcium aluminum silicate), stilbite (hydrated sodium calcium aluminum silicate) or thomsonite (hydrated sodium calcium aluminum silicate), or combinations thereof. In certain embodiments of the invention, the zeolites for use herein include chabazite, clinoptilolite, or a combination thereof.

For the cementitious compositions of the present embodiments, zeolite is a component of a base mix. The amount of zeolite in the base mix is between 0% and 100% by weight. In additional embodiments of the cementitious compositions, zeolite is present in an amount ranging between any of and including any of 5%, 10%, 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, or 95% by weight of base mix.

Cementitious material: The term "cementitious," as used herein, means having the properties of cement. The cementitious material comprises cement, fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, or a combination thereof. A cementitious material of the present invention is a component of the base mix. The amount of cementitious material in the base mix is between 0% and 100% by weight and, in additional embodiments, the cementitious material is present in an amount ranging between any of and including any of 5%, 10%, 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, or 95% by weight of base mix.

A variety of cements can be used with the present embodiments, including but not limited to hydraulic cements. Hydraulic cements set and harden by reaction with water and include Portland cements such as oil well cements, for example, pozzolan cements, gypsum cements, aluminous cements, silica cements, and alkaline cements. The physical properties of cement are a direct result of the chemical composition of cement, which composition includes tricalcium silicate, dicalcium silicate, tricalcium aluminate, tetracalcium aluminoferrite, and gypsum. By adjusting the amounts of each component the physical properties of cement are adjusted because of differences in the time and rate of hydration of each of the components.

OilΛvell cements are generally classified as follows:

• API Class A cement is used in general as an ordinary grade of cement when no particular properties are required. Class A cement is used to depths of up to 6000 feet (1830 meters).

• API Class B cement is also used to depths of up to 6000 feet (1830 meters) and has a moderate resistance to sulfates.

• API Class C cement is used to depths of up to 6000 feet (1830 meters) and is a high initial resistance cement.

• API Class G cement is a base cement used to depths of up to 8000 feet (2440 meters), and is used with accelerators or retarders for different depths and temperatures.

• API Class H cement is similar to Class G cement, however, with a higher mixture density.

API Class B, C, G, and H cements can be obtained in grades that have high sulfate resistance. Typically in permafrost areas, API Class A, G, or H cements are used.

Further cements useful for embodiments of the present invention include ASTM Portland cements such as:

• Type I Portland cement is a general purpose cement useful for most purposes.

• Type II Portland cement is used where sulfate concentrations in groundwaters are higher than normal. Type II Portland cement will usually generate less heat at a slower rate than Type I Portland cement.

• Type III Portland cement provides high strength at an early set time. It has more tricalcium silicate than Type I Portland cement. It is used when the structure must be ready for use quickly.

• Type IA, HA, and IIIA Portland cements are types of air-entraining Portland cements. They are the same as Types I, II, and III Portland cements, respectively, with the addition of small quantities of air-entraining materials interground with clinker to produce discrete air bubbles. These cements have improved resistance to freezing and thawing damage.

• Type IV Portland cement is used where the rate and amount of heat generated during setting must be minimized such as for use in massive concrete structures. Type IV Portland cement contains about one half of the tricalcium silicate and tricalciutn aluminate and twice the amount of dicalcium silicate as Type I Portland cement.

Type V Portland cement is a sulfate-resistant cement used where soil or groundwater has a high sulfate content. Type V Portland cement has a low tricalcium aluminate content.

Typically in permafrost areas, Type I, III, or V Portland cements are used. API class C cement is similar to ASTM Type III Portland cement, however API does not allow grinding aids to be added to the cement during the grinding process whereas ASTM type cements have grinding aids added.

In general, since API Class C and ASTM Type III Portland cements are made specifically to generate early strength, they also generate a high heat of hydration and would not typically be selected for the present embodiments. However, cementing conditions may dictate a need for an early strength cement that would set at a lower temperature and, under such conditions, the cited types of cements may be selected for uses herein.

The fly ash included in embodiments of the present invention may be any commercially available fly ash. Fly ash is produced by the combustion of powdered coal with a forced draft. The fly ash is carried by flue gases and is recovered, for example, by electrostatic precipitators. Class C fly ash is commercially available from Halliburton Energy Services, Duncan, Oklahoma. Class F fly ash is commercially available from Halliburton Energy Services as Pozmix^® A or from Ashcor Technologies Limited (Calgary, Alberta, Canada). For compositions of the present embodiments, fly ash is present in the base mix in an amount between 0% and 100% by weight. In additional embodiments of the cementitious compositions, fly ash is present in an amount ranging between any of and including any of 5%, 10%, 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, or 95% by weight of base mix.

Slag is commercially available from Lonestar Industries Inc. (Indianapolis, Indiana, USA). Fumed silica is commercially available from Fritz Industries (Mesquite, Texas, USA) and Elkem Group (Oslo, Norway). Diatomaceous earth is commercially available from Western Pozzolan Corp. (Doyle, Nevada, USA), calcined shale is commercially available from TXI (Houston, Texas, USA), metakaolin is commercially available from ISG Resources (South Jordan, Utah, USA) and Advanced Cement Technologies, LLC. (Blaine, Washington, USA), and rice husk ash is commercially available from Hi Rise Exports Private Ltd. (Calcutta, India) and Kittiya (U-Thaimai, Utaitanee, Thailand).

Source of Calcium Ion for Class F Fly Ash and Certain Cementitious Materials: Compositions of the present embodiments that include Class F fly ash and other pozzolanic cementitious materials such as diatomaceous earth, fumed silica, calcined shale, metakaolin, and rice husk ash also include a source of calcium ion. For compositions of the present embodiments that include added calcium, calcium ion is present in an amount of from about 5% to about 50% by weight of Class F fly ash or pozzolan and, in certain embodiments, calcium is present in an amount ranging between any of and including any of 10%, 15%, 20%, 25%, 30%, 35%, 40% or 45% by weight of Class F fly ash or pozzolan. A source of calcium may be an activator, or a calcium salt such as a salt having an anion containing a Group 4A, Group 5A, Group 6A, or Group 7A element, or a combination thereof, of the Periodic Table of the Elements. That is, carbonates, carboxylates, silicates, nitrates, nitrites, phosphates, sulfates, sulfites, and halide salts of calcium in addition to oxides and hydroxides of calcium provide a source of calcium, for example.

Optional Additives: Additives known to those of ordinary skill in the art may be included in the cementitious compositions of the present embodiments. Additives are typically blended with a base mix or may be added to a cementitious slurry. An additive may comprise an accelerator, a retarder, an activator, a defoamer, silica, a fluid loss control additive, a flow enhancing agent, a dispersant, or a combination thereof, for example. Selection of the type and amount of additive largely depends on the nature and composition of the set composition, and those of ordinary skill in the art will understand how to select a suitable type and amount of additive for compositions herein.

An activator is a catalyst for the setting reaction and may be one or more of lime, lime hydrate, calcium hydroxide, calcium chloride, sodium silicate, sodium fluoride, sodium silicofluoride, magnesium silicofluoride, zinc silicofiuoride, sodium carbonate, potassium carbonate, sodium hydroxide, potassium hydroxide, sodium sulfate, or hydrates thereof, for example. Setting accelerators increase the rate of the setting reaction and may be added to the cementitious compositions. Setting accelerators include compounds such as sodium chloride, sodium sulfate, sodium aluminate, sodium carbonate, calcium sulfate, calcium carbonate, aluminum sulfate, potassium sulfate, potassium carbonate and alums, or a combination thereof, for example.

A retarder slows the setting time of a cementitious composition, thereby allowing for control of the setting time of such a composition. Controlling the setting time is desirable to allow flexibility to adjust to wellbore conditions, or to adjust for adequate removal of drilling or spacer fluids. Retarders include a lignosulfonate, an organic acid having an α- hydroxy group such as citric acid, tartaric acid or gluconic acid, salts thereof, or a combination thereof, for example. Further examples of carboxylic acids that retard the setting time include carboxylic acids such as malic acid, lactic acid, combinations thereof, as well as alkaline earth metal salts thereof such as calcium, potassium, or barium salts, and the like. The salt of the organic acid may have a cation containing an element from Group IA or Group 2 A of the Periodic Table of the Elements.

Defoamers include agents such as polypropylene glycol, polypropylene glycol on diatomaceous earth, or a mixture of polypropylene glycol, olefin oil and hydrophobically modified silica.

Dispersants include agents such as salts of sulfonated naphthalene-formaldehyde condensate, salts of sulfonated naphthalene-formaldehyde condensate combined with polyvinylpyrolidone, salts of sulfonated melamine-formaldehyde condensates, salts of polyether polycarboxylate, sulfonic acid esters, carbohydrate esters or modified lignosulfonates, for example. The salt may have a cation containing an element from Group IA or Group 2A of the Periodic Table of the Elements, and in certain embodiments the salt is a calcium or a sodium salt, or a combination thereof.

Carrier Fluids: Carrier fluids suitable for use in the compositions of the present embodiments comprise aqueous fluids, oil-based and synthetic-based fluids, emulsions, or mixtures thereof. Exemplary aqueous fluids include but are not limited to water and water- based gels. When the carrier fluid comprises water, the water can be fresh water, unsaturated salt solution, including brines and seawater, and saturated salt solution. The carrier fluid is present in an amount of from about 20% to about 200% by weight of the base mix for cementitious materials. In further embodiments, the carrier fluid is present in an amount of from about 100% to about 200%, from about 50% to about 150% or from about 100% to about 125% by weight of the base mix for cementitious materials. Exemplary oil-based carrier fluids include but are not limited to canola oil, kerosene, diesel oil, fish oil, mineral oil, sunflower oil, corn oil, soy oil, olive oil, cottonseed oil, peanut oil and paraffin. Exemplary synthetic-based fluids include but are not limited to esters, olefins or ethers, e.g., esters having a C₂-C₁₂ alcohol portion and a C₁₆-C₂₄ carboxylic acid portion, olefins having a C₆-C₁₈ linear internal portion, or ethers having a C₆-C₂₄ portion. Those of ordinary skill in the art will understand that the carrier fluid for the compositions as provided herein depends upon the properties desired for the compositions, as well as the cost, availability, temperature, stability, viscosity, clarity, and the like of the carrier fluid, and further that when non-aqueous carrier fluids are used, the composition is expected to be exposed to an aqueous fluid in the well for the composition to set. For example, such aqueous fluids may come from the cementitious slurry or from the permafrost or waterwell formation.

Setting Conditions: Setting of the cementitious compositions of the present embodiments may occur under a variety of conditions including variations in time and temperature. For applications using PVC pipe as casing, the setting temperature is below about 176 ⁰F (80 ⁰C). Setting temperatures of about 15 ⁰F to about 175 ⁰F (-9.4 ⁰C to 79.4 ⁰C) are appropriate for setting of the present compositions. In further embodiments, a temperature ranging between any of and including any of 15 ⁰F (-9.4 ⁰C), 30 ⁰F (-1.1 ⁰C), 50 ⁰F (10.0 ⁰F), 70 ⁰F (21.1 ⁰C), 90 ⁰F (32.2 ⁰C), 110 ⁰F (43.3 ⁰C), 130 ⁰F (54.4 ⁰C), 140 ⁰F (60.0 ⁰C), 150 ⁰F (65.6 ⁰C), 160 ⁰F (71.1 ⁰C), 170 ⁰F (76.7 ⁰C), or 175 ⁰F (79.4 ⁰C) is appropriate for setting of the present compositions. A target setting time for embodiments of the present invention is adjusted for the time needed to pump the cement into place. A target setting time for a cementitious composition of the present invention is adjusted such that the composition remains fluid for about 2 to about 6 hours to allow placing behind casing materials, and then sets within an acceptable time period such as a day.

The compositions may comprise a slurry density of about 10 pounds per gallon (1200 kilograms per cubic meter) to about 16 pounds per gallon (1920 kilograms per cubic meter). In further embodiments, the compositions may comprise a slurry density ranging between any of and including any of about 11 ppg (1320 Kg/m³), 11.5 ppg (1380 Kg/m³), 12.0 ppg (1440 Kg/m³) 12.5 ppg (1500 Kg/m³), 13.0 ppg (1560 Kg/m³), 13.5 ppg (1584 Kg/m³), 14.0 ppg (1680 Kg/m³), 14.5 ppg (1740 Kg/m³), 15.0 ppg (1800 Kg/m3), 15.5 ppg (1860 Kg/m3), and 16.0 ppg (1920 Kg/m3).

In a further embodiment of the present invention, the method of performing a cementing operation in a permafrost zone or a waterwell zone, the zone penetrated by a wellbore, comprises placing a cementitious composition into the zone, the cementitious composition comprising a base mix of cement and zeolite, and a water-based carrier fluid; and allowing the cementitious composition to set therein. In another embodiment of the method, the cementitious composition comprises a base mix of fly ash and zeolite, and a water-based carrier fluid.

The following example is illustrative of the method of lowering the maximum temperature of setting of a cementitious composition while increasing compressive strength. Slurries in the following examples were prepared, and compressive strengths were measured, according to API recommended practice for testing well cements as described in API Recommended Practice 1OB, 22nd edition, Dec. 1997.

Example

According to the present example slurry samples were prepared using standard API mixing procedure (API Recommended Practice 1OB, 22nd edition, Dec. 1997) and include the components set forth in Table 1. Zeolite (chabazite) was obtained from the C2C Corporation (Calgary, Canada) and mined from Arizona; Class C Fly Ash was obtained from Halliburton Energy Services, Duncan, Oklahoma; Premium Plus cement (API Class C cement) was obtained from Lehigh Inland Cement Limited (Edmonton, Alberta, Canada); and Class C fly ash retarder (sodium citrate) was obtained from Fritz Industries Inc. (Mesquite, TX).

The density of compositions 1-4 was 15.1 ppg (1812 Kg/m³), 14.7 ppg (1764 Kg/m³), 14.3 ppg (1716 Kg/m³) and 15.0 ppg (1800 Kg/m³), respectively. The water-to- solids ratio was 0.4 (40% water) for compositions 1 and 2 and 0.5 (50% water) for compositions 3 and 4.

A sufficient amount of each slurry of compositions 1-4 was prepared to fill a glass vacuum flask to the one liter mark and a temperature recording thermocouple device (SAPAC Temprecord HI, precision temperature recorder (Monitor Company, Modesto, California)) was placed into the slurry. The top of the flask was sealed to ensure that no heat was lost. The flask was then placed in a 5 gallon bucket surrounded by polystyrene to maintain a constant external atmosphere. The temperature recorders provided the temperature of the slurry as it hydrated. Temperature data are provided for 4 days for compositions 1, 2 and 4 in FIGS. 1, 2, and 4 respectively. Temperature data are provided for 9 days for composition 3 in FIG. 3. The beginning temperature, the maximum temperature reached during setting, and the difference between the two temperatures is provided in Table 2 for compositions 1-4. Compressive strengths were obtained using an Ultrasonic Cement Analyzer (Halliburton Energy Services, Duncan, OK) at three days of setting time and are provided in Table 2. Table 2. Compressive Strengths and Temperature Rise During Setting

As shown by the data of Table 2, the presence of zeolite in the base mix provides for a decrease in the temperature change from the beginning of the setting reaction to the maximum temperature achieved during setting. Further, the compositions having zeolite present have increased compressive strength at three days as compared to compositions lacking zeolite. Thus, the results of the present example demonstrate that the presence of zeolite in a cementitious slurry provides a lower maximum temperature for the setting reaction while simultaneously providing greater compressive strength to the set composition as compared to a slurry not having zeolite present.

Other embodiments of the present invention will be apparent to those skilled in the art from a consideration of this specification or practice of the embodiments disclosed herein. However, the foregoing specification is considered merely exemplary of the present invention with the true scope and spirit of the invention being indicated by the following claims.

The references cited herein, to the extent that they provide exemplary procedural or other details supplementary to those set forth herein, are specifically incorporated by reference.

As used herein and unless otherwise indicated, the terms "a" and "an" are taken to mean "one", "at least one" or "one or more".

Claims

WHAT IS CLAIMED IS:

1. A method of performing a cementing operation in a permafrost zone or a waterwell zone, comprising: placing a cementitious composition into the zone, the cementitious composition comprising: a base mix of cementitious material and zeolite, and a carrier fluid; and allowing the cementitious composition to set therein.

2. The method of Claim 1 wherein the cementing operation is primary cementing.

3. The method of Claim 1 wherein the cementing operation is remedial cementing.

4. The method of Claim 1 wherein the zeolite is present in the base mix in an amount of from about 5% to about 95% by weight of the base mix.

5. The method of Claim 1 wherein the zeolite is present in the base mix in an amount of from about 5% to about 50% by weight of the base mix.

6. The method of Claim 1 wherein the zeolite is present in the base mix in an amount of from about 20% to about 40% by weight of the base mix.

7. The method of Claim 1 wherein the cementitious material comprises cement, Hy ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, or a combination thereof.

8. The method of Claim 7 wherein the cementitious material comprises cement.

9. The method of Claim 7 wherein the cementitious material comprises Class C fly ash.

10. The method of Claim 7 wherein the cementitious material comprises a combination of cement and fly ash.

11. The method of Claim 1 wherein the zeolite is represented by the formula:

Ma/_n[(AlO₂)_a(SiO₂)_b] ^• xH₂0

where

M represents one or more cations selected from the group consisting of Na₅ K₅ Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CHs)₃NH₅ (CH3)4 N, Ga₅ Ge and P; n represents the cation valence; the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5; and x represents the moles of water entrained into the zeolite framework.

12. The method of Claim 1 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.

13. The method of Claim 1 wherein the cementitious composition comprises fly ash and the composition further includes a retarder.

14. The method of Claim 1 wherein the carrier fluid comprises a water-based carrier fluid.

15. The method of Claim 1 wherein the carrier fluid comprises an oil-based carrier fluid.

16. The method of Claim 1 wherein the cementitious composition further comprises an additive, wherein the additive comprises an accelerator, a retarder, an activator, a defoamer or a combination thereof.

17. The method of claim 16 wherein the additive is a retarder and the retarder is a lignosulfonate.

18. The method of claim 1 further comprising foaming the cementitious composition to form a foamed cementitious composition.

19. A method of performing a cementing operation in a permafrost zone or a waterwell zone, comprising: placing a cementitious composition into the zone, the cementitious composition comprising: a base mix of cement and zeolite, and a water-based carrier fluid; and allowing the cementitious composition to set therein.

20. A method of performing a cementing operation in a permafrost zone or a waterwell zone, comprising: placing a cementitious composition into the zone, the cementitious composition comprising: a base mix of fly ash and zeolite, and a water-based carrier fluid; and allowing the cementitious composition to set therein.