WO2006096255A2 - Thermoplastic film having metallic nanoparticle coating - Google Patents
Thermoplastic film having metallic nanoparticle coating Download PDFInfo
- Publication number
- WO2006096255A2 WO2006096255A2 PCT/US2006/002990 US2006002990W WO2006096255A2 WO 2006096255 A2 WO2006096255 A2 WO 2006096255A2 US 2006002990 W US2006002990 W US 2006002990W WO 2006096255 A2 WO2006096255 A2 WO 2006096255A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- nanoparticles
- optical film
- metallic
- stretched
- Prior art date
Abstract
Description
Claims