WO2008083243A1

WO2008083243A1 - Tire compositions and components containing free-flowing filler compositions

Info

Publication number: WO2008083243A1
Application number: PCT/US2007/088985
Authority: WO
Inventors: W. Michael York; Richard W. Cruse; Janna Jaeckel; Eric Raymond Pohl; Prashant G. Joshi
Original assignee: Continental Ag
Priority date: 2006-12-28
Filing date: 2007-12-27
Publication date: 2008-07-10
Also published as: ES2373344T3; EP2099859A1; US20080161460A1; EP2099859A4; US7968635B2; ATE523557T1; EP2099859B1

Abstract

Free-flowing filler compositions containing silated cyclic core polysulfide coupling agents, and rubber and tire compositions containing the filler compositions.

Description

TIRE COMPOSITIONS AND COMPONENTS CONTAINING FREE-FLOWING FILLER COMPOSITIONS

The present application is directed to an invention which was developed pursuant to a joint research agreement within the meaning of 35 U.S.C.§103(c). The joint research agreement dated May 7, 2001 as amended, between Continental AG, and General Electric Company, on behalf of GE Advanced Materials, Silicones Division, now Momentive Performance Materials

Inc.

CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to U.S. Application Serial No. 11/617,678 filed

December 28, 2006, the content of which is incorporated herein by reference in its entirety.

The present application is related to the following applications, filed on December 28, 2006, with the disclosures of each of the applications being incorporated by reference herein in their entireties: Application No. 11/617,663, filed December 28, 2006, entitled Tire Compositions And

Components Containing Silated Core Polysulfides.

Application No. 11/617,649, filed December 28, 2006, entitled Tire Compositions And Components Containing Free-Flowing Filler Compositions.

Application No. 11/617,683, filed December 28, 2006, entitled Tire Compositions And Components Containing Silated Cyclic Core Polysufides.

Application No. 11/617,659, filed December 28, 2006, entitled Tire Compositions and Components Containing Blocked Mercaptosilane Coupling Agent.

Application No. 11/648,460, filed December 28, 2006, entitled Free-Flowing Filler Composition And Rubber Composition Containing Same. Application No. 11/647,903, filed December 28, 2006, entitled Free-Flowing Filler

Composition And Rubber Composition Containing Same.

Application No. 11/647,780, filed December 28, 2006, entitled Blocked Mercaptosilane Coupling Agents, Process For Making And Uses In Rubber.

Application No. 11/648,287, filed December 28, 2006, entitled Silated Core Polysulfides, Their Preparation And Use In Filled Elastomer Compositions.

Application No. 11/647,901, filed December 28, 2006, entitled Silated Cyclic Core Polysulfides, Their Preparation And Use In Filled Elastomer Compositions. 1. Field of the Invention

The present invention generally relates to filler compositions, more particularly, to free- flowing filler compositions containing, or derived from, silated cyclic core polysulfides, and to tire compositions and tire components containing the filler composition. 2. Background of the Invention

Fuel economies and the need to protect the environment are economic and societal priorities. As a result, it has become desirable to produce elastomers with good mechanical properties so that they can be used in the form of rubber compositions usable for the construction of tires with improved properties, having in particular reduced rolling resistance.

To this end, numerous solutions have been proposed, such as, for example, the use of coupling, starring or functionalizing agents with reinforcing filler to modify elastomers with the goal of obtaining a good interaction between the modified elastomer and the reinforcing filler. In order to obtain the optimum reinforcement properties imparted by a filler, the filler is preferably present in the elastomeric matrix in a final form which is both as finely divided as possible and distributed as homogeneously as possible.

Without being bound by theory, filler particles tend to attract to one another and agglomerate within the elastomeric matrix. As such, there is a reduction in the number of filler- elastomer bonds created during the mixing process. As a result of these interactions the consistency of the rubber composition increases and makes processing more difficult.

Rubber compositions reinforced with fillers, such as, aluminas or aluminum (oxide-

)hydroxides, of high dispersibility, and sulfur-vulcanizable diene rubber composition, reinforced with a special precipitated silica of the highly dispersible type, are know in the art. Use of these fillers makes it possible to obtain tires or treads with improved rolling resistance, without adversely affecting the other properties, in particular those of grip, endurance and wear resistance. Although the use of these specific, highly reinforcing, siliceous or aluminous fillers has reduced the difficulties of processing the rubber compositions that contain them, such rubber compositions are nevertheless more difficult to process than rubber compositions filled conventionally with carbon black.

In particular, it is necessary to use a coupling agent, also known as a bonding agent, the function of which is to provide the connection between the surface of the filler particles and the elastomer, while facilitating the dispersion of this filler within the elastomeric matrix.

Sulfur-containing coupling agents used for mineral-filled elastomers involve silanes in which two alkoxysilylalkyl groups are bound, each to one end of a chain of sulfur atoms. The two alkoxysilyl groups are bonded to the chain of sulfur atoms by two similar, and in most cases, identical, hydrocarbon fragments. The general silane structures just described, hereinafter referred to as "simple bis polysulfide silanes," usually contain a chain of three methylene groups as the two mediating hydrocarbon units. In some cases, the methylene chain is shorter, containing only one or two methylenes per chain. The use of these compounds is primarily as coupling agents for mineral-filled elastomers. These coupling agents function by chemically bonding silica or other mineral fillers to polymer when used in rubber applications. Without being bound by theory, it is believed that coupling is accomplished by chemical bond formation between the silane sulfur and the polymer and by hydrolysis of the alkoxysilyl groups and subsequent condensation with silica hydroxyl groups. It is further believed that the reaction of the silane sulfur with the polymer occurs when the S-S bonds are broken and the resulting fragment adds to the polymer. It is further believed that a single linkage to the polymer occurs for each silyl group bonded to the silica. This linkage contains a single, relatively weak C-S and/or S-S bond(s) that forms the weak link between the polymer and the silica. Under high stress, this single C-S and/or S-S linkages may break and therefore contribute to wear of the filled elastomer.

The use of polysulfide silanes coupling agents in the preparation of rubber is well known. These silanes contain two silicon atoms, each of which is bound to a disubstituted hydrocarbon group, and three other groups of which at least one is removable from silicon by hydrolysis. Two such hydrocarbon groups, each with their bound silyl group, are further bound to each end of a chain of at least two sulfur atoms. These structures thus contain two silicon atoms and a single, continuous chain of sulfur atoms of variable length.

Hydrocarbon core polysulfide silanes that feature a central molecular core isolated from the silicon in the molecule by sulfur-sulfur bonds are known in the art. Polysulfide silanes containing a core that is an aminoalkyl group separated from the silicon atom by a single sulfur and a polysulfide group and where the polysulfide group is bonded to the core at a secondary carbon atom are also known in the art. As well as core fragments in which only two polysulfide groups are attached to the core.

However, polysulfide groups that are attached directly to an aromatic core have reduced reactivity with the polymer (rubber). The aromatic core is sterically bulky which may inhibit the reaction. Compositions in which the polysulfides are attached directly to cyclic aliphatic fragments derived by vinyl cyclohexene contain more than one silated core and form large rings. The cyclohexyl core is sterically more hindered than the aromatic core and is less reactive. Although these compositions may be able to form more than one sulfur linkage to the polymer rubber for each attachment of the coupling agent to the silica through the silyl group, their effectiveness is low probably due to the low reactivity.

Without being bound by theory, the low reactivity is due to the attachment of the polysulfide to the secondary carbon of cyclic core structure. The positioning of the polysulfide group is not optimal for reaction with the accelerators and reaction with the polymer. The present invention overcomes the deficiencies of the aforementioned compositions involving silane coupling agents in several ways. The silanes of the present invention described herein are not limited to two silyl groups nor to one chain of sulfur atoms. In fact, the molecular architecture of the present invention includes multiple polysulfide chains which are oriented in a noncollinear configuration (i.e., branched, in the sense that the branch points occur within the carbon backbone interconnecting the polysulfide chains), and provide a novel configuration.

The fillers of the present invention have advantages over that in the prior art by providing multiple points of sulfur attachment to polymer per point of silicon attachment to filler. The silanes of the fillers described herein may be asymmetric with regard to the groups on the two ends of the sulfur chains. The silyl groups, rather than occurring at the ends of the molecule, tend to occur more centrally and are chemically bonded to the core through carbon-carbon, carbon-sulfur and carbon-silicon bonds. The carbon-sulfur bonds of the thio ester linkages (sulfide) are more stable than the sulfur-sulfur bonds of the disulfide or polysulfide functional groups. These thio ether groups are therefore less likely to react with the accelerators and curing agents or to decompose when subjected to high shear or temperatures normally associated with the mixing and curing of rubber compounds. The thio ether linkage also provide a convenient synthetic route for making the silanes of the present invention. The cyclic core also contains multiple polysulfide groups that are attached to ring by a divalent, straight chain alkylene group. The attachment of the polysulfide group to the primary carbon of the alkylene group decreases significantly the steric hindrance of the core, and increases the reactivity of the polysulfides with the polymer. In addition, the cyclic core orients these alkylene chains containing the polysulfide groups away from each other to further reduce the steric hindrance near the polysulfide groups. This distinction is what allows silane silicon to become and remain bonded (through the intermediacy of a sequence of covalent chemical bonds) to polymer at multiple points using the silanes of the present invention.

Also, without being bound by theory, silated core silanes of the present invention include a Y-core structure. This Y-core structure is believed to enable bonding the polymer at two different points or crosslinking on two different polymer chains, and also enables attachment, such as by bonding, to a filler.

SUMMARY OF THE INVENTION

In a first embodiment of the present invention, a preformed, free-flowing filler composition, such as for use in tire compositions, is provided which comprises: a) a filler; b) a first silane which is a silated cyclic-core polysulfϊde having the general formula

[Y'R'Sx-lmfG'CSR^iX^^JntG^otRVlp (Formula 1) wherein: each occurrence of G¹ is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species having from 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b -]_cR⁴[-(CH₂)_dS_x-]_e; (Formula 2) each occurrence of G² is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species of 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b -]_cR⁵[-(CH₂)_dS_x-]_e; (Formula 3) each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms; each occurrence of Y¹ and Y² is independently selected from silyl (-SiX¹X²X³), hydrogen, alkoxy (-OR⁶), carboxylic acid, ester (-C(=O)OR⁶), wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of R² is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups; each occurrence of R⁴ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e; each occurrence of R⁵ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of c + e and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e; each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(K))O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of X² and X³ is independently selected from hydrogen, R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, X¹, wherein X¹ is independently selected from the group consisting of -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, , m, n, o, p, and x, is independently given by a, c and e are 1 to about 3; b is 1 to about 5; d is 1 to about 5; m and p are 1 to about 100; n is 1 to about 15; o is 0 to about 10; and x is 1 to about 10; and, optionally, c) a second silane having the general formula

[X¹X²X³SiR¹S_xR³SiX¹X²X³] (Formula 4) wherein; each occurrence of R¹ and R³ are chosen independently from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups wherein one hydrogen atom was substituted with a silyl group (-SiX¹X²X³), wherein X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group and X² and X³ is independently selected from the group consisting of hydrogen, R⁶, X¹, and -OSi containing groups that result from the condensation of silanols.

In a second embodiment of the present invention, rubber compositions are provided, such as for use in a tire composition, comprising at least one rubber, at least one free-flowing filler composition of the present invention, a curative and, optionally, at least one other additive selected from the group consisting of sulfur compounds, activators, retarders, accelerators, processing additives, oils, plasticizers, tackifying resins, silicas, fillers, pigments, fatty acids, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents, reinforcing materials, and mixtures thereof. The present invention is also directed to tire compositions for forming a tire component, the compositions formed by combining at least a preformed free-flowing filler composition and at least one vulcanizable rubber selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, and random styrene-butadiene rubbers (SBR); the preformed free-flowing filler composition formed by combining at least an active filler and a first silane; the active filler including at least one of active filler selected from carbon blacks, silicas, silicon based fillers, and metal oxides present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts by weight is carbon black, silica, or a combination thereof; and the first silane comprising at least one silated cyclic core polysulfide having the general formula

[Y¹R¹S_x-]_m[G¹(SR²SiX¹X²X³)_a]_n[G²]o[R³Y²]_p wherein: each occurrence of G¹ is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species having from 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b-]_cR⁴[-(CH₂)_dS_x-]_e; each occurrence of G² is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species of 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b -]_cR⁵[-(CH₂)_dS_x-]_e; each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms; each occurrence of Y¹ and Y² is independently selected from consisting of silyl (-

SiX¹X²X³), hydrogen, alkoxy (-OR⁶), carboxylic acid, ester (-C(=O)OR⁶) wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of R² is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups; each occurrence of R⁴ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e; each occurrence of R⁵ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of c + e and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e; each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of X² and X³ is independently selected from hydrogen, R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, X¹, wherein X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, m, n, o, p, and x, is independently given by a, c and e are 1 to about 3; b is 1 to about 5; d is 1 to about 5; ; m and p are 1 to about 100; n is 1 to about 15; o is 0 to about 10; and x is 1 to about 10; and wherein the tire composition is formulated to be vulcanizable to form a tire component compound having a Shore A Hardness of not less than 40 and not greater than 95 and a glass- transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C.

The present invention is also directed to tires at least one component of which comprises cured tire compositions obtained from rubber compositions according to the present invention.

The present invention is also directed to tire components, cured and uncured, including, but not limited to, tire treads, including any tire component produced from any composition including at least a silated core polysulfide.

The examples presented herein demonstrate that the fillers of the present invention impart a desirable balance of physical properties (performance to mineral-filled elastomer compositions) and better wear characteristics to articles manufactured from these elastomers, including tires and tire components. Improvements in rolling resistance are also apparent for elastomers used in tire applications.

The compositions of the present invention exhibit excellent dispersion of filler and can achieve excellent workability, and improved productivity in vulcanization.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is further described in the detailed description that follows by way of non-limiting examples of exemplary embodiments of the present invention, wherein: Fig. 1 shows HPLC analysis of the product of Example 1.

DEFINITIONS

In describing and claiming the present invention, the following terminology will be used.

The term "coupling agent" as used herein includes an agent capable of establishing a sufficient chemical and/or physical connection between the filler and the elastomer. Such coupling agents have functional groups capable of bonding physically and/or chemically with the filler, for example, between a silicon atom of the coupling agent and the hydroxyl (OH) surface groups of the filler (e.g., surface silanols in the case of silica); and, for example, sulfur atoms which are capable of bonding physically and/or chemically with the elastomer.

The term "filler" as used herein includes a substance that is added to the elastomer to either extend the elastomer or to reinforce the elastomeric network. Reinforcing fillers are materials whose moduli are higher than the organic polymer of the elastomeric composition and are capable of absorbing stress from the organic polymer when the elastomer is strained. Fillers include fibers, particulates, and sheet-like structures and can be composed of inorganic minerals, organosilicon compounds, such as, by way of nonlimiting example, silanes, silicones, and polysiloxanes, and intermediates comprising monomers and reactive additives having a silicon atom, and any other molecule, oligomer, polymer or interpolymer which contains a silicon atom and a carbon atom, silicates, silica, clays, ceramics, carbon, organic polymers, diatomaceous earth. The filler of the present invention can be essentially inert to the silane with which it is admixed, or it can be reactive therewith.

The term "particulate filler" or "particulate composition" as used herein includes a particle or grouping of particles to form aggregates or agglomerates, including reinforcement filler or particles, including without limitation, those containing or made from organic molecules, oligomers, and/or polymers, e.g., poly(arylene ether) resins, or functionalized reinforcement filler or particle. The term functionalized is intended to include any particles treated with an organic molecule, polymer, oligomer, or otherwise (collectively, treating agent(s)), thereby chemically bonding the treating agent(s) to the particle. The particulate filler of the present invention can be essentially inert to the silane with which it is admixed, or it can be reactive therewith.

The term "carrier" as used herein includes a porous or high surface area filler that has a high adsorption or absorption capability and is capable of carrying up to 75 percent liquid silane while maintaining its free-flowing and dry properties. The carrier filler of the present invention is essentially inert to the silane and is capable of releasing or deabsorbing the liquid silane when added to the elastomeric composition.

The term "preformed" as used herein shall be understood to include a filler composition that is prepared prior to its addition to a rubber or mixture of rubbers. The term "rubber" includes natural or synthetic elastomers, including polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers and styrenebutadiene rubbers.

The term "tire compositions" includes those compositions useful for the manufacture of tires or tire components, and includes rubber compositions that include at least one rubber, a silane or a free-flowing filler composition containing, or derived from, silated core polysulfide, and at least one active filler such as, by way of nonlimiting example, carbon blacks, silicas, silicon based fillers, and metal oxides present either alone or in combination. For example, an active filler may be selected from the group described above (e.g., carbon blacks, silicas, silicon based fillers, and metal oxides) and may be, but does not have to be, present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts can be carbon black, silica, or some combination thereof, and wherein said compositions can be formulated so that they are vulcanizable to form a tire component compound. The tire component compounds may have a Shore A Hardness of not less than 40 and not greater than 95 and a glass-transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C. The Shore A Hardness is measured in accordance with DIN 53505. The glass-transition temperature Tg (E"_max) is measured in accordance with DIN 53513 with a specified temperature sweep of -80 ⁰C to +80 ⁰C and a specified compression of 10 + 0.2 % at 10 Hz.

DETAILED DESCRIPTIONS OF THE PRESENT INVENTION The free-flowing filler composition of the present invention is a preformed, free-flowing filler composition for use in a tire composition which comprises: a) a filler; b) a first silane which is a silated cyclic core polysulfide having the general formula

[Y¹R¹S_x-]_m[G¹(SR²-SiX¹X²X³)a]_n[G²]o[R³Y²]p (1) is provided, wherein each occurrence of G¹ is independently selected from polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species having from 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (2)

[(CH₂)_b-]_cR⁴[-(CH₂)_dS_x-]_e; (2) each occurrence of G² is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species of 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (3)

[(CH₂)_b -]_cR⁵[-(CH₂)_dS_x-]_e; (3) each occurrence of R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group; each occurrence of Y¹ and Y² is independently selected from, but not limited to silyl (- SiX¹X²X³), alkoxy (-OR⁶), hydrogen, carboxylic acid (-C(=O)OH), ester (-C(=O)OR⁶, in which R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups and the like; each occurrence of R² is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups; each occurrence of R⁴ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e; each occurrence of R⁵ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e; each occurrence of X¹ is independently selected from hydrolysable groups -Cl, -Br, -OH, - OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups; each occurrence of X² and X³ is independently selected from hydrogen, the members listed above for R⁶, the members listed above for X¹ and -OSi containing groups that result from the condensation of silanols; each occurrence of the subscripts, a, b, c, d, e, m, n, o, p, and x, is independently given by a is 1 to about 3; b is 1 to about 5; c is 1 to about 3; d is 1 to about 5; e is 1 to about 3; ; m is 1 to about 100, n is 1 to about 15; o is 0 to about 10; p is 1 to about 100, and x is 1 to about 10; and, optionally, c) a second silane having the general formula [X¹X²X³SiR¹S_xR³SiX¹X²X³] (4) wherein; each occurrence of each occurrence of R¹ and R³ are chosen independently from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups wherein one hydrogen atom was substituted with a silyl group, (-SiX¹X²X³), wherein X¹ is independently selected from -Cl, -Br, - OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to

20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group and X² and X³ is independently selected from hydrogen, R⁶, X¹, and -OSi containing groups that result from the condensation of silanols. The term, "heterocarbon", as used herein, refers to any hydrocarbon structure in which the carbon-carbon bonding backbone is interrupted by bonding to hetero atoms, such as atoms of nitrogen, sulfur, phosphorus and/or oxygen, or in which the carbon-carbon bonding backbone is interrupted by bonding to groups of atoms containing sulfur, nitrogen and/or oxygen, such as cyanurate (C3N3). Heterocarbon fragments also refer to any hydrocarbon in which a hydrogen or two or more hydrogens bonded to carbon are replaced with a sulfur, oxygen or nitrogen atom, such as a primary amine (-NH₂), and oxo (=0), and the like.

Thus, R⁴ and R⁵ include, but is not limited to cyclic, and/or polycyclic polyvalent aliphatic hydrocarbons that may be substituted with alkyl, alkenyl, alkynyl, aryl and/or aralkyl groups; cyclic and/or polycyclic polyvalent heterocarbon optionally containing ether functionality via oxygen atoms each of which is bound to two separate carbon atoms, polysulfϊde functionality, in which the polysulfϊde group (-S_x-) is bonded to two separate carbon atoms on G¹ or G² to form a ring, tertiary amine functionality via nitrogen atoms each of which is bound to three separate carbon atoms, cyano (CN) groups, and/or cyanurate (C₃N₃) groups; aromatic hydrocarbons; and arenes derived by substitution of the aforementioned aromatics with branched or straight chain alkyl, alkenyl, alkynyl, aryl and/or aralkyl groups.

As used herein, "alkyl" includes straight, branched and cyclic alkyl groups; "alkenyl" includes any straight, branched, or cyclic alkenyl group containing one or more carbon-carbon double bonds, where the point of substitution can be either at a carbon-carbon double bond or elsewhere in the group; and "alkynyl" includes any straight, branched, or cyclic alkynyl group containing one or more carbon-carbon triple bonds and optionally also one or more carbon- carbon double bonds as well, where the point of substitution can be either at a carbon-carbon triple bond, a carbon-carbon double bond, or elsewhere in the group. Examples of alkyls include, but are not limited to methyl, ethyl, propyl, isobutyl. Examples of alkenyls include, but are not limited to vinyl, propenyl, allyl, methallyl, ethylidenyl norbornane, ethylidene norbornyl, ethylidenyl norbornene, and ethylidene norbornenyl. Some examples of alkynyls include, but are not limited to acetylenyl, propargyl, and methylacetylenyl.

As used herein, "aryl" includes any aromatic hydrocarbon from which one hydrogen atom has been removed; "aralkyl" includes any of the aforementioned alkyl groups in which one or more hydrogen atoms have been substituted by the same number of like and/or different aryl (as defined herein) substituents; and "arenyl" includes any of the aforementioned aryl groups in which one or more hydrogen atoms have been substituted by the same number of like and/or different alkyl (as defined herein) substituents. Some examples of aryls include, but are not limited to phenyl and naphthalenyl. Examples of aralkyls include, but are not limited to benzyl and phenethyl, and some examples of arenyls include, but are not limited to tolyl and xylyl. As used herein, "cyclic alkyl", "cyclic alkenyl", and "cyclic alkynyl" also include bicyclic, tricyclic, and higher cyclic structures, as well as the aforementioned cyclic structures further substituted with alkyl, alkenyl, and/or alkynyl groups. Representative examples include, but are not limited to norbornyl, norbornenyl, ethylnorbornyl, ethylnorbornenyl, cyclohexyl, ethylcyclohexyl, ethylcyclohexenyl, cyclohexylcyclohexyl, and cyclododecatrienyl, and the like. Representative examples of X¹ include, but are not limited to methoxy, ethoxy, propoxy, isopropoxy, butoxy, phenoxy, benzyloxy, hydroxy, chloro, and acetoxy. Representative examples of X² and X³ include the representative examples listed above for X¹ as well as hydrogen, methyl, ethyl, propyl, isopropyl, sec-butyl, phenyl, vinyl, cyclohexyl, and higher straight-chain alkyl, such as butyl, hexyl, octyl, lauryl, and octadecyl, and the like. Representative examples of R¹, R² and R³ include the terminal straight-chain alkyls further substituted terminally at the other end, such as -CH₂-, -CH₂CH₂-, -CH₂CH₂CH₂-, and -CH₂CH₂CH₂CH₂CH₂CH₂CH₂CH₂-, and their beta-substituted analogs, such as -CH₂(CH₂)_MCH(CH₃)-, where u is zero to 17; the structure derivable from methallyl chloride, -CH₂CH(CH₃)CH₂-; any of the structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH₂CH₂- and -CH₂CH₂(C₆H₄)CH(CH₃)-, where the notation C₆H₄ denotes a disubstituted benzene ring; any of the structures derivable from diallylether, such as -CH₂CH₂CH₂OCH₂CH₂CH₂- and -CH₂CH₂CH₂OCH₂CH(CH₃)-; any of the structures derivable from butadiene, such as -CH₂CH₂CH₂CH₂-, -CH₂CH₂CH(CH₃)-, and -CH₂CH(CH₂CH₃)-; any of the structures derivable from piperylene, such as -CH₂CH₂CH₂CH(CH₃)-, -CH₂CH₂CH(CH₂CH₃)-, and -CH₂CH(CH₂CH₂CH₃)-; any of the structures derivable from isoprene, such as -CH₂CH(CH₃)CH₂CH₂-, -CH₂CH(CH₃)CH(CH₃)-, -CH₂C(CH₃)(CH₂CH₃)-, -CH₂CH₂CH(CH₃)CH₂-, -CH₂CH₂C(CH₃)₂- and -CH₂CH[CH(CH₃)₂]-; any of the isomers of -CH₂CH₂-norbornyl-, -CH₂CH₂-CyClOhCXyI-; any of the diradicals obtainable from norbornane, cyclohexane, cyclopentane, tetrahydrodicyclopentadiene, or cyclododecene by loss of two hydrogen atoms; the structures derivable from limonene, -CH₂CH(4-methyl-l -C_OH^)CH₃, where the notation C₆H₉ denotes isomers of the trisubstituted cyclohexane ring lacking substitution in the 2 position; any of the monovinyl-containing structures derivable from trivinylcyclohexane, such as -CH₂CH₂(vinylC₆H₉)CH₂CH₂- and -CH₂CH₂(vinylC₆H₉)CH(CH₃)-, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the monounsaturated structures derivable from myrcene containing a trisubstituted C=C, such as -CH₂CH[CH₂CH₂CH=C(CH3)2]CH₂CH2-, -CH₂CH[CH₂CH₂CH=C(CH_S)₂]CH(CH₃)-,

-CH₂C[CH₂CH₂CH=C(CH_S)₂](CH₂CH₃)-, -CH₂CH₂CH[CH₂CH₂CH=C(CH₃)₂]CH₂-, -CH₂CH₂(C-)(CH₃)[CH₂CH₂CH=C(CH₃)₂], and -CH₂CH[CH(CH₃)[CH₂CH₂CH=C(CH₃)₂]]-; and any of the monounsaturated structures derivable from myrcene lacking a trisubstituted C=C, such as -CH₂CH(CH=CH₂)CH₂CH₂CH₂C(CH3)₂-, -CH₂CH(CH=CH₂)CH₂CH₂CH[CH(CH₃)₂]-, -CH₂C(=CH-CH₃)CH2CH₂CH₂C(CH₃)2-, -CH₂C(=CH-CH₃)CH₂CH₂CH[CH(CH3)₂]-, -CH2CH₂C(=CH₂)CH₂CH₂CH₂C(CH₃)₂-, -CH₂CH₂C(=CH₂)CH₂CH₂CH[CH(CH₃)2]-, -CH₂CH=C(CH₃)₂CH₂CH₂CH₂C(CH₃)₂-, and -CH₂CH=C(CH₃)₂CH₂CH₂CH[CH(CH₃)₂].

Representative examples of G¹ include, but are not limited to, structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH(CH₂-)-, -CH₂CH₂(C₆H₃-)CH₂CH₂-, and

-CH₂(CH-XC₆H₄)CH(CH₂-)-, where the notation C₆H₄ denotes a disubstituted benzene ring and C₆H₃- denotes a trisubstituted ring; any structures derivable from trivinylcyclohexane, such as -CH₂(CH-)(vinylC₆H₉)CH₂CH₂-; (-CH₂CH₂)₃C₆H9, and (-CH₂CH₂)₂C₆H₉CH(CH3)-, -CH₂(CH-)(vinylC₆H₉)(CH-)CH₂-, -CH₂CH₂C₆H₉[(CH-)CH₂-]₂, -CH(CH₃)C₆H₉[(CH-)CH₂-]₂, and C₆H₉[(CH-)CH₂-]₃, -CH₂(CH-)C₆H₉[CH₂CH₂-]₂, and

-CH₂(CH-)C₆H₉[CH(CH₃)-] [CH₂CH₂-], where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring.

Representative examples of G² include, but are not limited to, structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH₂CH₂-, -CH₂CH₂(C₆H₄)CH(CH₂-)-,-CH₂CH₂(C₆H₃- )CH₂CH₂-, -CH₂(CH-XC₆H₄)CH(CH₂-)-, where the notation C₆H₄ denotes a disubstituted benzene ring and C₆H₃- denotes a trisubstituted ring; any structures derivable from trivinylcyclohexane, such as -CH₂CH₂(vinylC₆H₉)CH₂CH₂-, (-CH₂CH₂)C₆H₉CH₂CH₃, -CH₂(CH-)(vinylC₆H₉)CH₂CH₂-, (-CH₂CH₂)₃C₆H₉, (-CH₂CH₂)₂C₆H₉CH(CH₃)-, -CH₂(CH-)(vinylC₆H₉)(CH-)CH₂-, -CH₂CH₂C₆H₉[(CH-)CH₂-]₂, -CH(CH₃)C₆H₉[(CH-)CH₂-]₂, C₆H₉[(CH-)CH₂-]₃, -CH₂(CH-)C₆H₉[CH₂CH₂-]₂, and

-CH₂(CH-)C₆H₉[CH(CH₃)-][CH₂CH₂-], where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring.

Representative examples of silated cyclic core polysulfide silanes of the present invention include any of the isomers of 4-(6-triethoxysilyl-3-thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; l-(6-triethoxysilyl-3-thiahexyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 2-(6-triethoxysilyl-3-thiahexyl)-l,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 4-( 1 -methyl-5-triethoxysilyl-2-thiapentyl)- 1 ,2-bis-( 1 -methyl-8- triethoxysilyl-2,3,4,5-tetrathiaoctyl)cyclohexane; 4-(5-triethoxysilyl-3-thiapentyl)-l,2-bis-(8- triethoxysilyl-3,4,5,6-tetrathiaoctyl)cyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)-l,2-bis-(7- triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)- 1 ,2-bis-(8- triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)-l,2-bis-(12- triethoxysilyl-3,4,5,6-tetrathiadodecyl)cyclohexane; 1 -(6-triethoxysilyl-3-thiahexyl)-2,4-bis-( 11 - triethoxysilyl-3,4,5,6-tetrathiaunidecyl)cyclohexane; 4-(3-triethoxysilyl- 1 -thiapropyl)- 1 ,2-bis- (13-triemoxysilyl-3,4,5,6,7-pentathiatridecyl)cyclohexane; 4-(6-diethoxymethylsilyl-3- thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(4-triethoxysilyl-2- thiabutyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(7-triethoxysilyl-3- thiaheptyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5-trithianonyl)cyclohexane; 4-(5-triethoxysilyl-2- thiapentyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)benzene; 4-(5-triethoxysilyl-2- thiapentyl)-l,2-bis-(9-triethoxysilyl-3,4,5-trithianonyl)benzene; 4-(5-triethoxysilyl-2-thiapentyl)- l,2-bis-(9-triethoxysilyl-3,4-dithianonyl)benzene; bis-2-[4-(3-triethoxysilyl-2-thiapropyl)-3-(9- triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl tetrasulfide; bis-2-[4-(3-triethoxysilyl-l- thiapropyl)-3-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl trisulfide; bis-2-[4-(3- triethoxysilyl-l-thiapropyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl disulfide; bis-2- [4-(6-triethoxysilyl-3-thiahexyl)-3-(9-triethoxysilyl-3,4,5-trithianonyl)phenyl]ethyl tetrasulfide; bis-2-[4-(6-triethoxysilyl-3-thiahexyl)-3-(9-triethoxysilyl-3,4,5-trithianonyl)nathyl]ethyl tetrasulfide; bis-2-[4-(4-diethoxymethylsilyl-2-thiabutyl)-3-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)phenyl] ethyl trisulfide; bis-2-[4-(l-methyl-5-triethoxysilyl-2-thiapentyl)-3-(7- triethoxysilyl-3,4-dithiaheptyl)cycloheptyl]ethyl disulfide; bis-2-[4-(4-triethoxysilyl-2- thiabutyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclooctyl]ethyl disulfide; bis-2-[4-(4- triethoxysilyl-2-thiabutyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclododecyl]ethyl disulfide, 4- (6-triethoxysilyl-3-thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 2-(6- triethoxysilyl-3-thiahexyl)-l,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; l-(6- triethoxysilyl-3-thiahexyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(6- triethoxysilyl-3-thiahexyl)- 1 ,2-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 2-(6- triethoxysilyl-3-thiahexyl)- 1 ,4-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 1 -(6- triethoxysilyl-3-thiahexyl)-2,4-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; and mixtures thereof.

In another embodiment of the present invention the Formulae (1), (2) and (3), are described wherein each occurrence of R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 5 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group; each occurrence of Y¹ and Y² is chosen independently from silyl (- SiX',X²,X³); each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f - where f is an integer from about 0 to about 5; each occurrence of R⁴ is chosen independently from a polyvalent cyclic hydrocarbon fragment of 5 to about 12 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic alkyl or aryl in which a + c + e -1 hydrogens have been replaced; each occurrence of R⁵ is chosen independently from a polyvalent hydrocarbon fragment of 5 to about 12 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e, and include branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e - 1 hydrogens have been replaced; each occurrence of X¹ is chosen independently from f hydrolysable groups selected from -OH, and -OR⁶, in which R⁶ is any monovalent hydrocarbon group having from 1 to 5 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups; each occurrence of X² and X³ is chosen independently taken from R⁶ as defined for this embodiment and, any of X¹ as defined for this embodiment, and -OSi containing groups that result from the condensation of silanols; each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given by a is 1 to about 2; b is 1 to about 3; c is 1; d is 1 to about 3; e is 1; f is 0 to about 5; m is 1, n is 1 to about 10; o is 0 to about 1; p is 1, and x is 1 to about 6.

According to another embodiment of the present invention, 30 to 99 weight percent of the silated core polysulfϊde of the filler composition of the present invention is blended with 70 to 1 weight percent of another silane, including silanes of the structure represented in Formula (4)

[X¹X²X³SiR¹S_xR³SiX¹X²X³] (4) wherein each occurrence of each occurrence of R¹ and R³ are chosen independently from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a silyl group, (-SiX¹X²X³), wherein X¹ is chosen independently from any of hydrolysable groups selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, in which R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group and X² and X³ is independently taken from hydrogen, R⁶ as defined for this embodiment, any of X¹ as defined above, and -OSi containing groups that result from the condensation of silanols. This mixture of the silated core polysulfide of Formula (1) and the other silanes of Formula (4) correspond to a weight ratio about 0.43 to 99. In another embodiment, the mixture of the silated core polysulfϊde of Formula (1) and the other silanes of Formula (4) are in a weight ratio of about 1 to 19. Representative examples of this silane described by Formula (4) are listed in U. S. Patent

3,842,111, which is incorporated herein by reference, and include bis-(3-triethoxysilylpropyl) disulfide; bis-(3-triethoxysilylpropyl) trisulfide; bis-(3-triethoxysilylpropyl) tetrasulfide; bis(3- triethoxysilylpropyl) pentasulfide; bis-(3-diethoyxmethylsilypropyl) disulfide; bis- triethoxysilylmethyl disulfide; bis-(4-triethoxysilylbenzyl) disulfide; bis-(3- triethoxysilylphenyl) disulfide; and the like. The bonding of sulfur to a methylene group on R⁴ and R⁵ is desired because the methylene group mitigates excessive steric interactions between the silane and the filler and polymer. Two successive methylene groups mitigate steric interactions even further and also add flexibility to the chemical structure of the silane, thereby enhancing its ability to accommodate the positional and orientational constraints imposed by the morphologies of the surfaces of both the rubber and filler at the interphase, at the molecular level. The silane flexibility becomes increasingly important as the total number of silicon and sulfur atoms bound to G¹ and G² increases from 3 to 4 and beyond. Structures in which the polysulfide group is bonded directly to secondary and tertiary carbon atoms, ring structures, especially aromatic structures, are rigid and sterically hindered. The accelerators and curatives cannot readily orient themselves with the polysulfide group to affect reaction and the silated core polysulfide cannot readily orient itself to meet available binding sites on silica and polymer. This would tend to leave sulfur groups unbound to polymer, thereby reducing the efficiency by which the principle of multiple bonding of silane to polymer via multiple sulfur groups on silane, is realized. The use of a sulfide group to attach the silyl group to the core, -S-R²SiX¹X²X³, provides a convenient and cost effective way to bond the silyl group to the core. The sulfide group is less reactive than the polysulfide groups of the present invention and therefore is less likely to be broken during the curing of the rubbers containing the silated cyclic core polysulfides. The sulfide linkage of the silyl group to the core also makes it easier synthesize molecules with different lengths of the R² relative to R¹ and R³ and therefore to optimize the chemical structure of the silated cyclic core polysulfides to achieve bonding between the inorganic filler, such as silica, and the rubber.

The function of the other silanes in the filler is to occupy sites on the surface of the silica which aid in dispersing the silica and coupling with the polymer. Fillers of the present invention can be used as carriers for liquid silanes and reinforcing fillers for elastomers in which the silated core polysulfide is capable of reacting or bonding with the surface of the elastomers. The fillers that are used as carrier should be non-reactive with the silated core polysulfide. The non-reactive nature of the fillers is demonstrated by ability of the silated core polysulfide to be extracted at greater than 50 percent of the loaded silane using an organic solvent. The extraction procedure is given in U. S. Patent 6,005,027, which is incorporated herein by reference. Carriers include, but are not limited to, porous organic polymers, carbon black, diatomaceous earth, and silicas that are characterized by relatively low differential of less than 1.3 between the infrared absorbance at 3502 cm^"2 of the silica when taken at 105 ⁰C and when taken at 500 ⁰C, as described in U. S. Patent 6,005,027. In one embodiment, the amount of silated core polysulfide and, optionally, the other silanes of Formula (4) that can be loaded on the carrier is between 0.1 and 70 percent by weight. In another embodiment, the silated core polysulfide and, optionally, the other silanes of Formula (4) can be loaded on the carrier at concentrations between 10 and 50 percent by weight. In yet another embodiment, the filler is a particulate filler. Reinforcing fillers useful in the present invention include fillers in which the silanes are reactive with the surface of the filler. Representative examples of the fillers include, but are not limited to, inorganic fillers, siliceous fillers, metal oxides such as silica (pyrogenic and/or precipitated), titanium, aluminosilicate and alumina, clays and talc, and the like. Particulate, precipitated silica is useful for such purpose, particularly when the silica has reactive surface silanols. In one embodiment of the present invention, a combination of 0.1 to 20 percent silated core polysulfide and optionally, the other silanes of Formula (4) and 80 to 99.9 percent silica or other reinforcing fillers is utilized to reinforce various rubber products, including treads for tires. In another embodiment, a filler is comprising from about 0.5 to about 10 percent silated core polysulfide of Formula (1) and optionally a second silane of Formula (4) and about 90 to about 99.5 weight percent particulate filler. In another embodiment of the present invention, alumina can be used alone with the silated core polysulfide, or in combination with silica and the silated core polysulfide. The term, alumina, can be described herein as aluminum oxide, or Al₂O₃. In a further embodiment of the present invention, the fillers may be in the hydrated form.

Mercury porosity surface area is the specific surface area determined by mercury porosimetry. Using this method, mercury is penetrated into the pores of the sample after a thermal treatment to remove volatiles. Set up conditions may be suitably described as using about a 100 mg sample; removing volatiles during about 2 hours at about 105 ⁰C and ambient atmospheric pressure; ambient to about 2000 bars pressure measuring range. Such evaluation may be performed according to the method described in Winslow, Shapiro in ASTM bulletin, p.39 (1959) or according to DIN 66133. For such an evaluation, a CARLO-ERBA Porosimeter 2000 might be used. The average mercury porosity specific surface area for the silica should be in a range of about 100 to about 300 m²/g.

The pore size distribution for the silica, alumina and aluminosilicate according to such mercury porosity evaluation is considered herein to be such that five percent or less of its pores have a diameter of less than about 10 nm, about 60 to about 90 percent of its pores have a diameter of about 10 to about 100 nm, about 10 to about 30 percent of its pores have a diameter at about 100 to about 1,000 nm, and about 5 to about 20 percent of its pores have a diameter of greater than about 1,000 nm.

Silica might be expected to have an average ultimate particle size, for example, in the range of about 10 to about 50 nm as determined by the electron microscope, although the silica particles may be even smaller, or possibly larger, in size. Various commercially available silicas may be considered for use in this invention such as, from PPG Industries under the HI-SIL trademark with designations HI-SIL 210, 243, etc.; silicas available from Rhone-Poulenc, with, for example, designation of ZEOSIL 1165MP; silicas available from Degussa with, for example, designations VN2 and VN3, etc. and silicas commercially available from Huber having, for example, a designation of HUBERSIL7 8745.

In one embodiment of the invention, the filler compositions may utilize the silated cyclic core polysulfide with fillers such as silica, alumina and/or aluminosilicates in combination with carbon black reinforcing pigments. In another embodiment of the invention, the filler compositions may comprise a particulate filler mix of about 15 to about 95 weight percent of the siliceous filler, and about 5 to about 85 weight percent carbon black, and 0.1 to about 19 weight percent of silated cyclic core polysulfide, wherein the carbon black has a CTAB value in a range of about 80 to about 150. In yet another embodiment of the invention, it is desirable to use a weight ratio of siliceous fillers to carbon black of at least about 3 to 1. In yet another embodiment, a weight ratio of siliceous fillers to carbon black of at least about 10 to 1. In still another embodiment of the present invention, the weight ratio of siliceous fillers to carbon black may range from about 3 to 1 to about 30 to 1.

In one embodiment of the invention, the filler can be comprised of about 60 to about 95 weight percent of silica, alumina and/or aluminosilicate and, correspondingly, about 40 to about 5 weight percent carbon black and from about 0.1 to 20 weight percent silated cyclic core polysulfide of the present invention and optionally a second silane, with the proviso that the mixture of the components add up to 100 percent. The siliceous filler and carbon black may be pre-blended or blended together in the manufacture of the vulcanized rubber.

The filler can be essentially inert to the silane with which it is admixed as is the case with carbon black or organic polymers, or it can be reactive therewith, e.g., the case with carriers possessing metal hydroxyl surface functionality, e.g., silicas and other siliceous particulates which possess surface silanol functionality.

According to yet another embodiment of the present invention, a rubber composition, such as for use in tires, is provided comprising: (a) a rubber component;

(b) a free-flowing filler composition with a silated cyclic core polysulfide of Formula

(i);

(c) and, optionally a second silane, such as silanes according to Formula (4).

The silated cyclic core polysulfide silane(s) and optionally other silane coupling agents may be premixed or pre-reacted with the filler particles prior to the addition to the rubber mix, or added to a rubber mix during the rubber and filler processing, or mixing stages. If the silated cyclic core polysulfide silanes and, optionally, other silanes and filler are added separately to the rubber mix during the rubber and filler mixing, or processing stage, it is considered that the silated cyclic core polysulfide silane(s) then combine(s) in an in-situ fashion with the filler. In accordance with another embodiment of the present invention an uncured or cured rubber composition, such as for use in tires, is provided comprising:

(a) a rubber component;

(b) a free-flowing filler composition with a silated cyclic core polysulfide of Formula (1) (c)optionally, silanes, such as silanes of Formula (4);

(d) curatives; and

(e) optionally, other additives.

The rubbers useful with the filler compositions of the present invention include sulfur vulcanizable rubbers including conjugated diene homopolymers and copolymers, and copolymers of at least one conjugated diene and aromatic vinyl compound. Suitable organic polymers for preparation of rubber compositions are well known in the art and are described in various textbooks including The Vanderbilt Rubber Handbook, Ohm, R.F., R.T. Vanderbilt Company, Inc., 1990 and in the Manual for the Rubber Industry, Kemperman, T and Koch, S. Jr., Bayer AG, LeverKusen, 1993, the disclosures of which are incorporated by reference herein in their entireties.

In one embodiment of the present invention, the polymer for use herein is solution- prepared styrene-butadiene rubber (SSBR). In another embodiment of the invention, the solution prepared SSBR typically has a bound styrene content in a range of about 5 to about 50 percent, and about 9 to about 36 percent in another embodiment. According to another embodiment of the present invention, the polymer may be selected from the group consisting of emulsion- prepared styrene-butadiene rubber (ESBR), natural rubber (NR), ethylene-propylene copolymers and terpolymers (EP, EPDM), acrylonitrile-butadiene rubber (NBR), polybutadiene (BR), and the like, and mixtures thereof.

In one embodiment, the rubber composition is comprised of at least one diene-based elastomer, or rubber. Suitable conjugated dienes include, but are not limited to, isoprene and 1,3-butadiene and suitable vinyl aromatic compounds include, but are not limited to, styrene and alpha methyl styrene. Polybutadiene may be characterized as existing primarily, typically about 90% by weight, in the cis-l,4-butadiene form, but other compositions may also be used for the purposes described herein. Thus, the rubber is a sulfur curable rubber. Such diene based elastomer, or rubber, may be selected, for example, from at least one of cis-l,4-polyisoprene rubber (natural and/or synthetic), emulsion polymerization prepared styrene/butadiene copolymer rubber, organic solution polymerization prepared styrene/butadiene rubber, 3,4-polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubber, cis-l,4-polybutadiene, medium vinyl polybutadiene rubber (35-50 percent vinyl), high vinyl polybutadiene rubber (50- 75 percent vinyl), styrene/isoprene copolymers, emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber. For some applications, an emulsion polymerization derived styrene/butadiene (ESBR) having a relatively conventional styrene content of about 20 to 28 percent bound styrene, or an ESBR having a medium to relatively high bound styrene content of about 30 to 45 percent may be used.

Emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubbers containing 2 to 40 weight percent bound acrylonitrile in the terpolymer are also contemplated as diene based rubbers for use in this invention. The vulcanized rubber composition should contain a sufficient amount of filler composition to contribute a reasonably high modulus and high resistance to tear. In one embodiment of the present invention, the combined weight of the filler composition may be as low as about 5 to about 120 parts per hundred parts (phr), or about 5 to about 100 phr. In another embodiment, the combined weight of the filler composition is from about 25 to about 85 phr and at least one precipitated silica is utilized as a filler in another embodiment. The silica may be characterized by having a BET surface area, as measured using nitrogen gas, in the range of about 40 to about 600 m²/g. In one embodiment of the invention, the silica has a BET surface area in a range of about 50 to about 300 m²/g. The BET method of measuring surface area is described in the Journal of the American Chemical Society, Volume 60, page 304 (1930). The silica typically may also be characterized by having a dibutylphthalate (DBP) absorption value in a range of about 100 to about 350, and more usually about 150 to about 300. Further, the silica, as well as the aforesaid alumina and aluminosilicate, may be expected to have a CTAB surface area in a range of about 100 to about 220. The CTAB surface area is the external surface area as evaluated by cetyl trimethylammonium bromide with a pH of about 9. The method is described in ASTM D 3849.

The rubber compositions of the present invention may be prepared by mixing one or more of the silated cyclic core polysulfide silanes and optionally other silanes with the organic polymer before, during or after the compounding of the filler composition into the organic polymer. The silated cyclic core polysulfide silanes and optionally other silanes also may be added before or during the compounding of the filler composition into the organic polymer, because these silanes facilitate and improve the dispersion of the filler. In another embodiment, the total amount of silated cyclic core polysulfide silane present in the resulting combination should be about 0.05 to about 25 parts by weight per hundred parts by weight of organic polymer (phr); and 1 to 10 phr in another embodiment. In yet another embodiment, fillers can be used in quantities ranging from about 5 to about 120 phr, about 5 to about 100 phr, or about 25 to about 80 phr, and still in another embodiment from about 25 to about 110, or about 25 to about 105.

In practice, sulfur vulcanized rubber products typically are prepared by thermomechanically mixing rubber and various ingredients in a sequentially step-wise manner followed by shaping and curing the compounded rubber to form a vulcanized product. First, for the aforesaid mixing of the rubber and various ingredients, typically exclusive of sulfur and sulfur vulcanization accelerators (collectively, curing agents), the rubber(s) and various rubber compounding ingredients typically are blended in at least one, and often (in the case of silica filled low rolling resistance tires) two or more, preparatory thermomechanical mixing stage(s) in suitable mixers. Such preparatory mixing is referred to as nonproductive mixing or non- productive mixing steps or stages. Such preparatory mixing usually is conducted at temperatures of about 140 ⁰C to about 200 ⁰C, and for some compositions, about 150 ⁰C to about 170 ⁰C. Subsequent to such preparatory mix stages, in a final mixing stage, sometimes referred to as a productive mix stage, curing agents, and possibly one or more additional ingredients, are mixed with the rubber compound or composition, at lower temperatures of typically about 50 ⁰C to about 130 ⁰C in order to prevent or retard premature curing of the sulfur curable rubber, sometimes referred to as scorching. The rubber mixture, also referred to as a rubber compound or composition, typically is allowed to cool, sometimes after or during a process intermediate mill mixing, between the aforesaid various mixing steps, for example, to a temperature of about 50 ⁰C or lower. When it is desired to mold and to cure the rubber, the rubber is placed into the appropriate mold at a temperature of at least about 130 ⁰C and up to about 200 ⁰C which will cause the vulcanization of the rubber by the S-S bond-containing groups (i.e., disulfide, trisulfide, tetrasulfide, etc.; polysulfide) on the silated core polysulfide silanes and any other free sulfur sources in the rubber mixture.

Thermomechanical mixing refers to the phenomenon whereby under the high shear conditions in a rubber mixer, the shear forces and associated friction occurring as a result of mixing the rubber compound, or some blend of the rubber compound itself and rubber compounding ingredients in the high shear mixer, the temperature autogeneously increases, i.e. it "heats up". Several chemical reactions may occur at various steps in the mixing and curing processes. The first reaction is a relatively fast reaction and is considered herein to take place between the filler and the silicon alkoxide group of the silated cyclic core polysulfides. Such reaction may occur at a relatively low temperature such as, for example, at about 120 ⁰C. The second reaction is considered herein to be the reaction which takes place between the sulfur- containing portion of the silated cyclic core polysulfide silane, and the sulfur vulcanizable rubber at a higher temperature; for example, above about 140 ⁰C.

Another sulfur source may be used, for example, in the form of elemental sulfur, such as but not limited to S₈. A sulfur donor is considered herein as a sulfur containing compound which liberates free, or elemental sulfur, at a temperature in a range of about 140 ⁰C to about 190 ⁰C. Such sulfur donors may be, for example, although are not limited to, polysulfide vulcanization accelerators and organosilane polysulfides with at least two connecting sulfur atoms in its polysulfide bridge. The amount of free sulfur source addition to the mixture can be controlled or manipulated as a matter of choice relatively independently from the addition of the aforesaid silated cyclic core polysulfide silane. Thus, for example, the independent addition of a sulfur source may be manipulated by the amount of addition thereof and by the sequence of addition relative to the addition of other ingredients to the rubber mixture.

In one embodiment of the invention, the rubber composition may therefore comprise about 100 parts by weight rubber (phr) of at least one sulfur vulcanizable rubber selected from the group consisting of conjugated diene homopolymers and copolymers, and copolymers of at least one conjugated diene and aromatic vinyl compound, about 5 to 100 phr, preferably about 25 to 80 phr of at least one filler, up to about 5 phr curing agent, and about 0.05 to about 25 phr of at least one silated cyclic core polysulfide silane as described in the present invention.

In another embodiment, the filler composition comprises from about 1 to about 85 weight percent carbon black based on the total weight of the filler composition and up to about 20 parts by weight of at least one cyclic silated core polysulfide silane of the present invention based on the total weight of the filler composition, including about 2 to about 20 parts by weight of at least one cyclic silated core polysulfide silane of the present invention based on the total weight of the filler composition.

The rubber composition may be prepared by first blending rubber, filler and silated cyclic core polysulfide silane, or rubber, filler pretreated with all or a portion of the silated cyclic core polysulfide silane and any remaining silated cyclic core polysulfide silane, in a first thermomechanical mixing step to a temperature of about 140 ⁰C to about 200 ⁰C for about 2 to about 20 minutes. The fillers may be pretreated with all or a portion of the silated core polysulfide silane and any remaining silated cyclic core polysulfide silane, in a first thermomechanical mixing step to a temperature of about 140⁰C to about 200⁰C for about 4 to 15 minutes. Optionally, the curing agent is then added in another thermomechanical mixing step at a temperature of about 50 ⁰C and mixed for about 1 to about 30 minutes. The temperature is then heated again to between about 130⁰C and about 200⁰C and curing is accomplished in about 5 to about 60 minutes. In another embodiment of the present invention, the process may also comprise the additional steps of preparing an assembly of a tire or sulfur vulcanizable rubber with a tread comprised of the rubber composition prepared according to this invention and vulcanizing the assembly at a temperature in a range of about 130 ⁰C to about 200 ⁰C.

Other optional ingredients may be added in the rubber compositions of the present invention including curing aids, i.e. sulfur compounds, including activators, retarders and accelerators, processing additives such as oils, plasticizers, tackifying resins, silicas, other fillers, pigments, fatty acids, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents, reinforcing materials such as, for example, carbon black, and so forth. Such additives are selected based upon the intended use and on the sulfur vulcanizable material selected for use, and such selection is within the knowledge of one of skill in the art, as are the required amounts of such additives known to one of skill in the art.

The vulcanization may be conducted in the presence of additional sulfur vulcanizing agents. Examples of suitable sulfur vulcanizing agents include, for example elemental sulfur (free sulfur) or sulfur donating vulcanizing agents, for example, an amino disulfide, polymeric polysulfide or sulfur olefin adducts which are conventionally added in the final, productive, rubber composition mixing step. The sulfur vulcanizing agents, which are common in the art are used, or added in the productive mixing stage, in an amount ranging from about 0.4 to about 3 phr, or even, in some circumstances, up to about 8 phr, with a range of from about 1.5 to about 2.5 phr and all subranges therebetween in one embodiment from 2 to about 2.5 phr and all subranges therebetween in another embodiment.

Optionally, vulcanization accelerators, i.e., additional sulfur donors, may be used herein. It is appreciated that may include the following examples, benzothiazole, alkyl thiuram disulfide, guanidine derivatives and thiocarbamates. Representative of such accelerators can be, but not limited to, mercapto benzothiazole (MBT), tetramethyl thiuram disulfide(TMTD), tetramethyl thiuram monosulfide (TMTM), benzothiazole disulfide (MBTS), diphenylguanidine (DPG), zinc dithiocarbamate (ZBEC), alkylphenoldisulfide, zinc iso-propyl xanthate (ZIX), N-dicyclohexyl-2-benzothiazolesulfenamide (DCBS), N-cyclohexyl-2-benzothiazolesulfenamide (CBS), N-tert-buyl-2-benzothiazolesulfenamide (TBBS), N-tert-buyl-2- benzothiazolesulfenimide (TBSI), tetrabenzylthiuram disulfide (TBzTD), tetraethylthiuram disulfide (TETD), N-oxydiethylenebenzothiazole-2-sulfenamide, N,N-diphenylthiourea, dithiocarbamylsulfenamide, N,N-diisopropylbenzothiozole-2-sulfenamide, zinc-2-mercaptotoluimidazole, dithiobis(N-methyl piperazine), dithiobis(N-beta-hydroxy ethyl piperazine) and dithiobis(dibenzyl amine). Other additional sulfur donors, may be, for example, thiuram and morpholine derivatives. Representative of such donors are, for example, but not limited to, dimorpholine disulfide, dimorpholine tetrasulfide, tetramethyl thiuram tetrasulfϊde, benzothiazyl-2,N-dithiomorpholide , thioplasts, dipentamethylenethiuram hexasulfide, and disulfidecaprolactam.

Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., a primary accelerator. Conventionally, a primary accelerator(s) is used in total amounts ranging from about 0.5 to about 4 phr and all subranges therebetween in one embodiment, and from about 0.8 to about 1.5, phr and all subranges therebetween in another embodiment. Combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts (of about 0.05 to about 3 phr and all subranges therebetween) in order to activate and to improve the properties of the vulcanizate. Delayed action accelerators may be used. Vulcanization retarders might also be used. Suitable types of accelerators are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. In one embodiment, the primary accelerator is a sulfenamide. If a secondary accelerator is used, the secondary accelerator can be a guanidine, dithiocarbamate and/or thiuram compounds. Preferably, tetrabenzylthiuram disulfide is utilized as a secondary accelerator in combination with N-tert-buyl-2-benzothiazolesulfenamide with or without diphenylguanidine. Tetrabenzylthiuram disulfide is a preferred accelerator as it does not lead to the production of nitrosating agents, such as, for example, tetramethylthiuram disulfide.

Typical amounts of tackifier resins, if used, comprise about 0.5 to about 10 phr and all subranges therebetween, usually about 1 to about 5 phr and all subranges therebetween. Typical amounts of processing aids comprise about 1 to about 50 phr and all subranges therebetween. Such processing aids can include, for example, aromatic, napthenic, and/or paraffϊnic processing oils. Typical amounts of antioxidants comprise about 1 to about 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in the Vanderbilt Rubber Handbook (1978), pages 344-346. Typical amounts of antiozonants, comprise about 1 to about 5 phr and all subranges therebetween. Typical amounts of fatty acids, if used, which can include stearic acid, comprise about 0.5 to about 3 phr and all subranges therebetween. Typical amounts of zinc oxide comprise about 2 to about 5 phr. Typical amounts of waxes comprise about 1 to about 5 phr and all subranges therebetween. Often microcrystalline waxes are used. Typical amounts of peptizers comprise about 0.1 to about 1 phr and all subranges therebetween. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide.

The rubber compositions of this invention can be used for various purposes. For example, it can be used for various tire compounds, weather stripping, and shoe soles. In one embodiment of the present invention, the rubber compositions described herein are particularly useful in tire treads, but may also be used for all other parts of the tire as well. The tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art.

Preferred compositions include those compositions useful for the manufacture of tires or tire components, including vehicle tires, and include rubber compositions that include at least one vulcanizable rubber and at least one preformed filler. The fillers included in the preformed filler can include, by way of nonlimiting example, carbon blacks, silicas, silicon based fillers, and metal oxides present either alone or in combinations. For example, an active filler may be selected from the group described above (e.g., carbon blacks, silicas, silicon based fillers, and metal oxides) and may be, but does not have to be, present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts can be carbon black, silica, or some combination thereof, and wherein said compositions can be formulated so that they are vulcanizable to form a tire component compound. The tire component compounds may have a Shore A Hardness of not less than 40 and not greater than 95 and a glass-transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C. The Shore A Hardness is measured in accordance with DIN 53505. The glass-transition temperature Tg (E"_max) is measured in accordance with DIN 53513 with a specified temperature sweep of -80 ⁰C to +80 ⁰C and a specified compression of 10 + 0.2 % at 10 Hz. Preferably, the rubber comprises vulcanizable rubbers selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, random styrene-butadiene rubbers (SBR), and mixtures thereof. Moreover, an active filler includes a filler that is interactive with the rubber or tire composition and itself, and changes properties of the rubber or tire composition.

All references cited are specifically incorporated herein by reference as they are relevant to the present invention.

EXAMPLES

The examples presented below demonstrate significant advantages of silated cyclic core polysulfides described herein relative those of the currently practiced art, and their performance as coupling agents in silica-filled rubber. Example 1

Preparation of (6-triethoxysilyl-3-thia-l-hexyl)-bis- (7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane, related oliogmers and bis-(3- triethoxysilylpropyDpolysulfϊde mixture. This example illustrates the preparation of a silated cyclic core disulfide from a core containing three vinyl groups through the formation of an intermediate thioacetate silane. The tris-(4-oxo-3-thiapentyl)cyclohexane was prepared by the reaction of thioacetic acid with trivinylcyclohexane. Into a 5 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, condenser, and air inlet were charged 1,2,4-trivinylcyclohexane (779 grams, 4.8 moles) and t-butyl peroxide (8.0 grams, 0.055 mole). Freshly distilled thioacetic acid (1297 grams, 16.8 moles) was added by means of an addition funnel over a period of 30 minutes. The temperature rose from room temperature to 59 ⁰C. The reaction mixture was allowed to cool to room temperature, tert-butyl peroxide (25.3 grams, 0.173 moles) was added in two increments and the reaction mixture was heated overnight at 75 ⁰C. After cooling to 42 ⁰C, air was bubbled into the reaction mixture and an exotherm was observed. The mixture was stirred overnight at 75 ⁰C and then cooled to room temperature. The reaction mixture was stripped to remove any low boiling species under reduced pressure and a maximum temperature of 135 ⁰C to give the final product (1,866 grams, 4.77 moles). The yield was 99 percent. The l,2,4-tris-(2-mercaptoethyl)cyclohexane was prepared by removing the acyl group.

Into a 5 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, distilling head and condenser, and nitrogen inlet were charged tris-(4-oxo-3-thiapentyl)cyclohexane (1,866 grams, 4.77 moles) and absolute ethanol (1,219 grams, 26.5 moles). Sodium ethoxide in ethanol (99 grams of 21% sodium ethoxide, purchased from Aldrich Chemical) was added in five increments. The mixture was heated and the ethanol and ethyl acetate were removed. Ethanol (785 grams) was added and the ethyl acetate and ethanol were distilled from the mixture at atmospheric pressure. Ethanol (1,022 grams) was added to the mixture and the ethyl acetate, ethanol and low boiling components were distilled form the mixture under reduced pressure at 73 ⁰C. The mercaptan intermediate (1,161 grams, 4.5 moles) was used in the next step for the synthesis. The yield was 93 percent.

The bis-(2-mercaptoethyl)(6-triethylsilyl-3-thia-l-hexyl)cyclohexane was prepared by reaction of the trimercaptan intermediate with 3-chloropropyltriethyoxysilane. Into a 3 L, three- neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, condenser, air inlet and a sodium hydroxide scrubber, was charged l,2,4-tris-(2-mercaptoethyl)cyclohexane (450 grams, 1.7 moles). Sodium ethoxide in ethanol (421 grams of 21% sodium ethoxide, purchased from Aldrich Chemical) was added over two hours. 3-Chloropropyltriethoxysilane (410 grams, 1.7 moles) was added slowly over a period of 2 hours and then heated at reflux for 14 hours. An additional aliquot of 3- chloropropyltriethoxysilane (42.5 grams, 0.18 mole) was added, heated for 2.5 hours at 79 ⁰C, cooled and then filtered. The crude product was distilled under reduced pressure. The fraction that boiled between 191 and 215 ⁰C was collected (343 grams, 0.73 mole) and used in the next step of the synthesis. The product yield was 43 percent. The product, (6-triethoxysilyl-3-thia-l-hexyl)-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane, was prepared by reacting the silated dimercaptan intermediated with sulfur and 3-chloropropyltriethoxysilane. Into a 3 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, distilling head and condenser, and nitrogen inlet were charged bis-(2-mercaptoethyl)(6-triethylsilyl-3-thia- l-hexyl)cyclohexane (326 grams, 0.7 mole), sodium ethoxide in ethanol (451 grams of 21% sodium ethoxide, purchased from Aldrich Chemical), sulfur powder (45 grams, 1.4 moles) and absolute ethanol (352 grams) and refluxed for 3 hours. 3-Chloropropyltriethoxysilane (336 grams, 1.4 moles) was added, refluxed for 72 hours, cooled and filtered using a glass fritted filter with a 25 - 50 micron pore size. The solids were washed with toluene, the organic layers combined and stripped to remove the lights. The final product (635 grams, 0.7 mole) was analyzed by HPLC. The chromatograph, shown in Figure 1, indicated a mixture of monomeric and oligomeric products.

One isomer of (6-triethoxysilyl-3-thia- 1 -hexyl)-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane has the following structure:

Example 2

Preparation of (6-triethoxysilyl-3-thia- 1 -hexyl)-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane, related oliogmers and bis-

(3-triethoxvsilvlpropvl)polysulfide mixture. The dimercaptan silane intermediate, (6-triethoxysilyl-3-thia-l-hexyl)-bis-(2- mercaptoethyl)cyclohexane, was prepared by the procedure described in Example 1.

The product, (6-triethoxysilyl-3-thia-l-hexyl)-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane, related oliogmers and bis-(3-triethoxysilylpropyl)polysulfide mixture, was prepared by reacting the dimercaptan silane with base, sulfur and 3- chloropropyltriethoxysilane. Into a 2 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, distilling head and condenser, and nitrogen inlet were charged bis-(2-mercaptoethyl)(6-triethylsilyl-3-thia-l- hexyl)cyclohexane (249.7 grams, 0.53 mole), sodium ethoxide in ethanol (345.2 grams of 21% sodium ethoxide, purchased from Aldrich Chemical), sulfur powder (102.5 grams, 3.2 moles) and absolute ethanol (250grams) and refluxed for 24 hours. 3-Chloropropyltriethoxysilane (256.5 grams, 1.07 moles) was added, refluxed for 72 hours, cooled and then filtered using a 3.5 micron asbestocel filter. The final product (487.4 grams, 0.47 mole, 88 percent yield) was analyzed by HPLC. The chromatograph indicated a mixture of products.

One isomer of (6-triethoxysilyl-3-thia-l-hexyl)-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl) cyclohexane has the following structure:

Comparative Example A-C, Examples 3-5 The Use of Silanes in Low Rolling Resistant Tire Tread Formulation.

A model low rolling resistance passenger tire tread formulation as described in Table 1 and a mix procedure were used to evaluate representative examples of the silanes of the present invention. The silane in Example 2 was mixed as follows in a "B" BANBUR Y® (Farrell Corp.) mixer with a 103 cu. in. (1,690 cc) chamber volume. The mixing of the rubber was done in two steps. The mixer was turned on with the mixer at 80 rpm and the cooling water at 71° C. The rubber polymers were added to the mixer and ram down mixed for 30 seconds. The silica and the other ingredients in Masterbatch of Table 1 except for the silane and the oils were added to the mixer and ram down mixed for 60 seconds. The mixer speed was reduced to 35 rpm and then the silane and oils of the Masterbatch were added to the mixer and ram down for 60 seconds. The mixer throat was dusted down and the ingredients ram down mixed until the temperature reached 149⁰C. The ingredients were then mixed for an addition 3 minutes and 30 seconds. The mixer speed was adjusted to hold the temperature between 152 and 157°C. The rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85⁰C to 88⁰C, and then allowed to cool to ambient temperature. In the second step, Masterbatch was recharged into the mixer. The mixer's speed was

80 rpm, the cooling water was set at 71⁰C and the batch pressure was set at 6MPa. The Masterbatch was ram down mixed for 30 seconds and then the temperature of the Masterbatch was brought up to 149°C, and then the mixer's speed was reduce to 32 rpm and the rubber was mixed for 3 minutes and 20 seconds at temperatures between 152 and 157°C. After mixing, the rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85°C to 88°C, and then allowed to cool to ambient temperature.

The rubber Masterbatch and the curatives were mixed on a 15 cm x 33 cm two roll mill that was heated to between 48°C and 52°C. The sulfur and accelerators were added to the rubber

(Masterbatch) and thoroughly mixed on the roll mill and allowed to form a sheet. The sheet was cooled to ambient conditions for 24 hours before it was cured. The curing condition was 16O⁰C for 20 minutes. The silated cyclic-core polysulfides from Examples 1 and 2 were compounded into the tire tread formulation according to the above procedure and their performance was compared to the performance of silanes which are practiced in the prior art, bis-(3-triethoxysilyl- l-propyl)disulfide (TESPD), bis-(3-triethoxysilyl-l -propyl) tetrasulfide (TESPT) and 1,2,4-tris- (7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane (TESHC), Comparative Examples A-C. The test procedures were described in the following ASTM methods:

Mooney Scorch ASTM D 1646

Mooney Viscosity ASTM D 1646

Oscillating Disc Rheometer (ODR) ASTM D2084 Storage Modulus, Loss Modulus,

Tensile and Elongation ASTM D412 and D224

DIN Abrasion DIN Procedure 53516

Heat Buildup ASTM D623

Percent Permanent Set ASTM D623 Shore A Hardness ASTM D2240

The results of this procedure are tabulated below in Table 1. TESPD = bis-(3-triethoxy silylpropyl) disulfide TESPT = bis-(3-triethoxy silylpropyl) tetrasulfide

TESHC = l,2,4-tris-(6-triethoxysilyl-3,4-dithiaheptyl)cyclohexane Table 1

Table 1, listing Comparative Examples A-C and Examples 3 -5, presents the performance parameters of silated cyclic-core polysulfϊde of the present invention, bis-(3-triethoxysilylpropyl) disulfide, bis-(3-triethoxysilylpropyl)tetrasulfide and l,2,4-tris(6-triethoxysilyl-3,4- dithiaheptyl)cyclohexane. The physical properties of the rubber compounded with silated cyclic- core polysulfides from Examples 1 and 2 are consistently and substantially higher than the control silanes.

The silated cyclic core polysulfϊde of the present invention impart higher performance to silica-filled elastomer compositions, including better coupling of the silica to the rubber, as illustrated by the higher reinforcement index. The better reinforcing indices translate into performance improvements for the elastomer compositions and articles manufactured from these elastomers.

Example 6

Zeosil 1165 MP silica from Rhone-Poulenc of Lyon, France (50 grams) with the following properties:

Characteristic Value

BET surface area 180 m²/g

CTAB surface area 160 m²/g

DOP adsorption 270 ml/100 grams Water loss at 105 ⁰C 6%

Loss on ignition at 1000 ⁰C 10.5%

SiO₂ 98.5%

Al₂O₃ 0.4% pH 6.5

is poured into a 1 liter wide-mouthed jar. The open jar is placed in a ventilated oven at 105⁰C and left for drying for 4 hours. The infrared absorption differential is 1.12. To the hot silica, the silated cyclic core polysulfide from Example 2 (50 grams) is added in one portion and the jar is closed and shaken manually for 30 seconds. The resulting compound is a dry, free-flowing solid that does not stick to the container walls.

The extraction test is performed in a 100 ml Soxhlet extraction apparatus equipped with a 250 round bottom flask. The silated core polysulfide and silica mixture (30 grams) is placed in a paper cartridge and acetone of dry analytical grade is placed in the flask. The extraction test is performed in 2 hours from reflux start. The flask is heated with a heating mantle to 88⁰C. The cartridge is dried in an explosion-proof oven at 110 ° to constant weight. The weight-loss is calculated as a percent of extractable silane.

The mixture of the silated cyclic core polysulfide from Example 2 and silica is an example of silica used as a carrier.

Example 7 Zeosil 1165 MP silica from Rhone-Poulenc of Lyon, France (50 grams) with the following properties:

Characteristic Value BET surface area 180 m²/g

CTAB surface area 160 m²/g

DOP adsorption 270 ml/100 grams

Water loss at 105 ⁰C 6%

Loss on ignition at 1000 ⁰C 10.5% SiO₂ 98.5%

Al₂O₃ 0.4% pH 6.5 is poured into a 1 liter wide-mouthed jar. To the silica, the silated cyclic core polysulfide from

Example 2 (3.5 grams) is added in one portion and the jar is closed and shaken manually for 10 minutes. The jar is opened and the silated cyclic core polysulfide and silica are heated to 140⁰C for 1 hour using a heating mantle and stirred vigorously using a mechanical mixer and metal stirring shaft. Heating the silica is intended to drive the reaction of the silated cyclic core polysulfide with the silica and to remove the ethanol that is formed. The resulting compound is a dry, free-flowing solid that does not stick to the container walls. It is an example of a mixture where the silated cyclic core polysulfide and silica have reacted to form an article where the two components are covalently bound to each other.

Example 8

SIPERNAT 22 silica from DeGussa AG of Frankfurt, Germany (50 grams) with the following properties:

Characteristic Value

BET surface area 180 m²/g

CTAB surface area 160 m²/g

DOP adsorption 300 ml/100 grams Water loss at 105 ⁰C 6%

Loss on ignition at 1000 ⁰C 11%

SiO₂ 98%

Al₂O₃ 0% pH 6.0

is poured into a 1 liter wide-mouthed jar. To the silica, the silated cyclic-core polysulfide from Example 1 (5.3 grams) is added in one portion and the jar is closed and shaken manually for 10 minutes. The jar is opened and the silated cyclic core polysulfide and silica are heated to 140°C for 1 hour using a heating mantle and stirred vigorously using a mechanical mixer and metal stirring shaft. Heating the silica is intended to drive the reaction of the silated cyclic core polysulfide with the silica and to remove the ethanol that is formed.

The resulting compound is a dry, free-flowing solid that does not stick to the container walls. It is an example of a mixture where the silated cyclic core polysulfide and silica have reacted to form an article where the two components are covalently bound to each other.

Example 9

N330 Carbon Black from Columbian Chemical in Marietta, Georgia (100 grams) with the following properties: Characteristic Value

BET surface area 8⁰3^ m ^~7^2/g

CTAB surface area 82 m²/g

Iodine number 82 m JV-Ig is poured into a 1 liter wide-mouthed jar. The open jar containing the N330 carbon black is placed in a ventilated oven at 120°C and left for drying for 2 hours. To the hot carbon black, the silated cyclic core polysulfide from Example 2 (50 grams) is added in one portion and the jar is closed and shaken manually for 10 minutes. The resulting compound is a dry and free-flowing black powder.

The extraction test is performed in a 100 ml Soxhlet extraction apparatus equipped with a 250 round bottom flask. The silated cyclic core polysulfide and carbon mixture (30 grams) is placed in a paper cartridge and acetone of dry analytical grade is placed in the flask. The extraction test is performed in 2 hours from reflux start. The flask is heated with a heating mantle to 88⁰C. The cartridge is dried in an explosion-proof oven at 110⁰C to constant weight.

The weight-loss is calculated as a percent of extractable silane. The mixture of the silated cyclic core polysulfide from Example 2 and carbon black is an example of filler used as a carrier. The N330 is a reinforcing filler for elastomeric compositions. After the deadsorption of the liquid silane from the carbon black in the elastomeric composition, the carbon black functions as a reinforcing filler.

Example 10 The Use of Silated Cyclic-Core Polysulfides and Silica Mixtures in Low Rolling Resistant Tire

Tread Formulation.

A model low rolling resistance passenger tire tread formulation that is described in Table 1, except that 12 phr silated cyclic-core polysulfide and silica mixture of Example 6 replaces the silane from Example 2 and the Ultrasil VN3 GR silica loading was adjusted to 79 phr, is used to evaluate the performance of the silated core polysulfide on a silica carrier. The rubber compound is prepared according to the mix procedure that is described in Example 3. The example illustrates the utility of a silated cyclic-core polysulfide on a silica carrier.

Example 11 The Use of Silated Cyclic-Core Polysulfides and Silica Mixtures in Low Rolling

Resistant Tire Tread Formulation.

A model low rolling resistance passenger tire tread formulation that is described in Table 1, except that 92 phr silated cyclic-core polysulfide and silica mixture of Example 7 replaces the silane from Example 2 and the Ultrasil VN3 GR silica, is used to evaluate the performance of the silated core polysulfide on a silica carrier. The rubber compound is prepared according to the mix procedure that is described in Example 3. The example illustrates the utility of a silated cyclic-core polysulfide that is preformed and has coupled to the silica filler.

Example 12 The Use of Silated Cyclic-Core Polysulfides and Silica Mixtures in Low Rolling

Resistant Tire Tread Formulation.

A model low rolling resistance passenger tire tread formulation that is described in Table 1, except that 94 phr silated cyclic-core polysulfide and silica mixture of Example 8 replaces the silane from Example 2 and the Ultrasil VN3 GR silica, is used to evaluate the performance of the silated cyclic-core polysulfide on a silica filler. The rubber compound is prepared according to the mix procedure that is described in Example 3. The example illustrates the utility of a silated cyclic-core polysulfide that is preformed and has coupled to the silica filler before addition to the rubber mix. Example 13

The Use of Silated Cyclic-Core Polysulfides and Carbon Black Mixture in Low Rolling

Resistant Tire Tread Formulation.

A model low rolling resistance passenger tire tread formulation that is described in Table 1, except that 18 phr silated cyclic core polysulfide and carbon black mixture of Example 9 replaces the silane from Example 2 and the 12 phr carbon black, is used to evaluate the performance of the silated core polysulfide on a carbon black carrier. The rubber compound is prepared according to the mix procedure that is described in Example 3. The example illustrates the utility of a silated cyclic-core polysulfide on a carbon black carrier. It is noted that the foregoing examples have been provided merely for the purpose of explanation and are in no way to be construed as limiting of the present invention. While the present invention has been described with reference to exemplary embodiments, it is understood that the words which have been used herein are words of description and illustration, rather than words of limitation. Changes may be made, within the purview of the appended claims, as presently stated and as amended, without departing from the scope and spirit of the present invention in its aspects. Although the present invention has been described herein with reference to particular means, materials and embodiments, the present invention is not intended to be limited to the particulars disclosed herein; rather, the present invention extends to all functionally equivalent structures, methods and uses, such as are within the scope of the appended claims.

Claims

What is claimed is:

1. A tire composition for forming a tire component, the composition formed by combining at least a preformed free-flowing filler composition and at least one vulcanizable rubber selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, and random styrene-butadiene rubbers (SBR); the preformed free-flowing filler composition formed by combining at least an active filler and a first silane; the active filler including at least one of active filler selected from carbon blacks, silicas, silicon based fillers, and metal oxides present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts by weight is carbon black, silica, or a combination thereof; and the first silane comprising at least one silated cyclic core polysulfide having the general formula

[YVS_x-UGkSI^SiX'x'x^_aMG'MR'Y^p wherein: each occurrence of G¹ is independently selected from a polyvalent cyclic hydrocarbon or polyvalent cyclic heterocarbon species having from 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b-]_cR⁵[-(CH₂)_dS_x-]_e; each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms; each occurrence of Y¹ and Y² is independently selected from consisting of silyl (- SiX¹X²X³), hydrogen, alkoxy (-OR⁶), carboxylic acid, ester (-C(=O)OR⁶) wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of R² is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups; each occurrence of R⁴ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e; each occurrence of R⁵ is independently selected from a polyvalent cyclic hydrocarbon fragment of 1 to about 28 carbon atom that was obtained by substitution of hydrogen atoms equal to the sum of c + e and include cyclic and polycyclic alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e -1 hydrogens have been replaced, or a polyvalent cyclic heterocarbon fragment from 1 to 27 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e; each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(K))O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of X² and X³ is independently selected from hydrogen, R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, X¹, wherein X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, m, n, o, p, and x, is independently given by a, c and e are 1 to about 3; b is 1 to about 5; d is 1 to about 5; ; m and p are 1 to about 100; n is 1 to about 15; o is 0 to about 10; and x is 1 to about 10; and wherein the tire composition is formulated to be vulcanizable to form a tire component compound having a Shore A Hardness of not less than 40 and not greater than 95 and a glass- transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C.

2. The tire composition of claim 1 wherein the preformed, free-flowing filler composition further comprises a second silane having the general formula

[X¹X²X³SiR¹S_xR³SiX¹X²X³] wherein each occurrence of R¹ and R³ are chosen independently from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups wherein one hydrogen atom was substituted with a silyl group, (-SiX¹X²X³), wherein X¹ is independently selected from -Cl, -Br, - OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group and X² and X³ is independently selected from hydrogen, R⁶, X¹, and -OSi containing groups that result from the condensation of silanols.

3. The tire composition of Claim 1 wherein the filler is chemically inert relative to silane.

4. The tire composition of Claim 1 wherein the filler is chemically reactive to the silane and silane is chemically bonded to said chemically reactive filler.

5. The tire composition of Claim 3 wherein the filler is carbon black.

6. The tire composition of Claim 4 wherein the chemically reactive filler possesses surface inorganic hydroxyl functionality.

7. The tire composition of Claim 6 wherein the chemically reactive filler is a siliceous material.

8. The tire composition of Claim 7 wherein the siliceous material is a silica.

9. The tire composition of Claim 2 wherein the filler is a mixture of filler chemically inert relative to at least one of the first silane or second silane and filler which is chemically reactive to at least one of the first silane or second silane and chemically bonded thereto.

10. The tire composition of Claim 9 wherein the inert filler is carbon black and the chemically reactive filler is a silica.

11. The tire composition of Claim 1 wherein the silated cyclic core polysulfide is any of the isomers of 4-(6-triethoxysilyl-3-thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; l-(6-triethoxysilyl-3-thiahexyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 2-(6-triethoxysilyl-3-thiahexyl)-l,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 4-( 1 -methyl-5-triethoxysilyl-2-thiapentyl)- 1 ,2-bis-(l -methyl-8- triethoxysilyl-2,3,4,5-tetrathiaoctyl)cyclohexane; 4-(5-triethoxysilyl-3-thiapentyl)-l,2-bis-(8- triethoxysilyl-S^^jo-tetrathiaoclyOcyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)- 1 ,2-bis-(7- triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)- 1 ,2-bis-(8- triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; 4-(6-triethoxysilyl-3-thiahexyl)-l,2-bis-(12- triethoxysilyl-3,4,5,6-tetrathiadodecyl)cyclohexane; l-(6-triethoxysilyl-3-thiahexyl)-2,4-bis-(l l- triethoxysilyl-3,4,5,6-tetrathiaunidecyl)cyclohexane; 4-(3-triethoxysilyl-l-thiapropyl)-l,2-bis- ( 13-triethoxysilyl-3,4,5,6,7-pentathiatridecyl)cyclohexane; 4-(6-diethoxymethylsilyl-3- thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(4-triethoxysilyl-2- thiabutyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(7-triethoxysilyl-3- thiaheptyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5-trithianonyl)cyclohexane; 4-(5-triethoxysilyl-2- thiapentyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)benzene; 4-(5-triethoxysilyl-2- thiapentyl)-l,2-bis-(9-triethoxysilyl-3,4,5-trithianonyl)benzene; 4-(5-triethoxysilyl-2-thiapentyl)- l,2-bis-(9-triethoxysilyl-3,4-dithianonyl)benzene; bis-2-[4-(3-triethoxysilyl-2-thiapropyl)-3-(9- triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl tetrasulfide; bis-2-[4-(3-triethoxysilyl- 1 - thiapropyl)-3-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl trisulfide; bis-2-[4-(3- triethoxysilyl-l-thiapropyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl disulfide; bis-2- [4-(6-triethoxysilyl-3-thiahexyl)-3-(9-triethoxysilyl-3,4,5-trithianonyl)phenyl]ethyl tetrasulfide; bis-2-[4-(6-triethoxysilyl-3-thiahexyl)-3-(9-triethoxysilyl-3,4,5-trithianonyl)nathyl]ethyl tetrasulfide; bis-2-[4-(4-diethoxymethylsilyl-2-thiabutyl)-3-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)phenyl]ethyl trisulfide; bis-2-[4-(l-methyl-5-triethoxysilyl-2-thiapentyl)-3-(7- triethoxysilyl-3,4-dithiaheptyl)cycloheptyl] ethyl disulfide; bis-2-[4-(4-triethoxysilyl-2- thiabutyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclooctyl]ethyl disulfide; bis-2-[4-(4- triethoxysilyl-2-thiabutyl)-3-(7-triethoxysilyl-3,4-dithiaheptyl)cyclododecyl]ethyl disulfide, 4- (6-triethoxysilyl-3-thiahexyl)-l,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 2-(6- triethoxysilyl-3-thiahexyl)-l,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; l-(6- triethoxysilyl-3-thiahexyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(6- triethoxysilyl-3-miahexyl)-l ^-bis-^-triethoxysilyl-S^-dithiaheptytycyclohexane; 2-(6- triethoxysilyl-S-thiahexyO-l^-bis-CT-triethoxysilyl-S^-dithiaheptyOcyclohexane; l-(6- triethoxysilyl-3-thiahexyl)-2,4-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; and mixtures thereof.

12. The tire composition of Claim 11 wherein the filler is chemically inert relative to silane.

13. The tire composition of Claim 11 wherein the filler is chemically reactive to the silane and silane is chemically bonded to said chemically reactive filler.

14. The tire composition of Claim 12 wherein the filler is carbon black.

15. The tire composition of Claim 13 wherein the chemically reactive filler possesses surface metal hydroxyl functionality

16. The tire composition of Claim 15 wherein the chemically reactive filler is a siliceous material.

17. The tire composition of Claim 16 wherein the siliceous material is a silica.

18. The tire composition of Claim 13 wherein the filler is a mixture of filler chemically inert relative to the silane and filler which is chemically reactive to the silane and chemically bonded thereto.

19. The tire composition of Claim 18 wherein the inert filler is carbon black and the chemically reactive filler is a silica.

20. The tire composition of Claim 2 containing from about 0.1 to 19 weight percent first silane or mixture of first silane and second silane.

21. The tire composition of Claim 2 containing from about 0.1 to 20 weight percent first silane or mixture of first silane and second silane.

22. The tire composition of Claim 2 containing about 0.1 to 70 weight percent first silane or mixture of first silane and second silane.

23. The tire composition of Claim 2 wherein the silane is a mixture of first silane and second silane in a weight ratio of from about 0.43 to about 99.

24. The tire composition of Claim 2 wherein the silane is a mixture of first silane and second silane in a weight ratio of from about 1 to about 19.

25. The tire composition of Claim 1 wherein the at least one vulcanizable rubber comprises emulsion polymerization derived styrene/butadiene having a styrene content of about 20 to about 28 weight percent.

26. The tire composition of Claim 25 wherein the emulsion polymerization derived styrene/butadiene has a styrene content of about 30 to about 45 weight percent.

27. The tire composition of Claim 1 wherein the at least one vulvanizable rubber comprises emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber containing from about 2 to about 40 weight percent acrylonitrile.

28.. The tire composition according to claim 1 wherein the silated cyclic core polysulfide comprises any isomer of (6-triethoxysilyl-3-thia-l-hexyl)-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane.

29. The tire composition according to claim 1 wherein the silated cyclic core polysulfide comprises any isomer of (6-triethoxysilyl-3-thia-l-hexyl)-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane.

30. The tire composition of Claim 1, further comprising curative and, optionally, at least one other additive selected from sulfur compounds, activators, retarders, accelerators, processing additives, oils, plasticizers, tackifying resins, silicas, fillers, pigments, fatty acids, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents, reinforcing materials, and mixtures thereof.

31. A tire at least one component of which comprises a cured rubber composition obtained from the tire composition of Claim 1.

32. A tire tread which comprises a cured rubber composition obtained from the rubber composition of Claim 1.

33. A tire component comprising a cured rubber composition obtained from the tire composition of claim 1.

34. An uncured tire component comprising a rubber composition obtained from the tire composition of claim 1.